3 Electromechanical Behaviour of Chitosan Based Electroactive Polymer

Authors: O. Ozdemir, Y. Seki, İ. Şen, K. Sever, M. Sarikanat, E. Akar, O. C. Yılmaz, B. O. Gürses, L. Cetin

Abstract:

Chitosan is a natural, nontoxic, polyelectrolyte, cheap polymer. In this study, chitosan based electroactive polymer (CBEAP) was fabricated. Electroactive properties of this polymer were investigated at different voltages. It exhibited excellent tip displacement at low voltages (1, 3, 5, 7 V). Tip displacement was increased as the applied voltage increased. Best tip displacement was investigated as 28 mm at 5V. Characterization of CBEAP was investigated by scanning electron microscope, X-ray diffraction and tensile testing. CBEAP exhibited desired electroactive properties at low voltages. It is suitable for using in artificial muscle and various robotic applications.

Keywords: Electroactive Polymer, chitosan, electroactive properties

Procedia PDF Downloads 325
2 An Investigation on Viscoelastic and Electrical Properties of Biopolymer-Based Composites

Authors: Y. Seki, İ. Şen, K. Sever, M. Sarikanat, Z. Yenier

Abstract:

It is known that Chitosan, as a natural polymer, has many excellent properties such as bicompotability, biodegradability and nontoxicity. Besides it has some limitations such as poor solubility in water and low conductivity in electrical devices and sensor applications. In order to improve electrical conductivity properties grapheme loading was conducted into chitosan. For this aim, chitosan solution was prepared in acidic condition and Graphene at different ratios was mixed with chitosan solution by the help of homogenizator. After film formation electrical conductivity values of chitosan and graphene loaded chitosan were determined. After grapheme loading into chitosan,solution significant increases in surface resistivity value of chitosan were observed. Besides variations on viscoeleastic properties with graphene loading was determined by dynamic mechanical analysis. Storage and Loss moduli were obtained for chitosan and grapheme loaded chitosan samples.

Keywords: Graphene, Electrical Conductivity, chitosan, viscoelastic properties

Procedia PDF Downloads 314
1 Evaluation of Vine Stem Waste as a Filler Material for High Density Polyethylene

Authors: O. Ozdemir, Y. Seki, A. Ç. Kılıç, M. Atagür, İ. Şen, K. Sever, Ö. Seydibeyoğlu, M. Sarikanat, N. Küçükdoğan

Abstract:

Cheap and abundant waste materials have been investigated as filler materials in thermoplastic polymers instead of wood- based materials because of deforestation. Vine stem, as an agricultural waste, was used as a filler material for a thermoplastic polymer, high-density polyethylene (HDPE) in this study. Agricultural waste of vine stem was collected from Manisa region, Turkey. Vine stem at different rations was used to reinforce HDPE. The effect of vine stem loading on tensile strength and Young’s modulus of composites were obtained. It was clearly observed that tensile strength and Young’s modulus of HDPE was increased by vine stem loading. Thermal stabilities of composites were obtained by using thermogravimetric analysis. Water absorption behavior of HDPE was improved by loading vine stem into HDPE. The crystallinity index values of neat HDPE and vine stem loaded HDPE composites were investigated byX-ray diffraction analysis. From this study, it was inferred that vine stem, as an agricultural waste, can be used as a filler material for HDPE.

Keywords: Composite Materials, Composite, high density polyethylene, waste filler

Procedia PDF Downloads 367