2 Preparation of Gold Nanoparticles Stabilized in Acid-Activated Montmorillonite for Nitrophenol Reduction

Authors: Fatima Ammari, Meriem Chenouf

Abstract:

Synthesis of gold nanoparticles (AuNPs) has attracted much attention since the pioneering discovery of the high catalytic activity of supported gold nanoparticles in the reaction of CO oxidation at low temperature. In this research field, we used montmorillonite pre-acidified under gentle conditions for AuNPs stabilization; using different loading percentage 1, 2 and 5%. The gold nanoparticles were obtained using chemical reduction method using NaBH4 as reductant agent. The obtained gold nanoparticles stabilized in acid-activated montmorillonite were used as catalysts for reduction of 4-nitrophenol to aminophenol with sodium borohydride at room temperature The UV-Vis results confirm directly the gold nanaoparticles formation. The XRD N2 adsorption and MET results showed the formation of gold nanoparticles in the pores of preacidified montmorillonite with an average size of 5.7nm. The reduction reaction of 4-nitrophenol into 4-aminophenol with NaBH4 catalyzed by Au°-montmorillonite catalyst exhibits remarkably a high activity; the reaction was completed within 4.5min.

Keywords: Nanoparticles, Gold, acid-activated montmorillonite

Procedia PDF Downloads 255
1 Synthesis of Gold Nanoparticles Stabilized in Na-Montmorillonite for Nitrophenol Reduction

Authors: Fatima Ammari, Meriem Chenouf

Abstract:

Synthesis of gold nano particles has attracted much attention since the pioneering discovery of the high catalytic activity of supported gold nano particles in the reaction of CO oxidation at low temperature. In this research field, we used Na-montmorillonite for gold nanoparticles stabilization; different loading percentage 1, 2 and 5%. The gold nano particles were obtained using chemical reduction method using NaBH4 as reductant agent. The obtained gold nano particles Au-mont stabilized in Na-montmorillonite were used as catalysts for reduction of 4-nitrophenol to aminophenol with sodium borohydride at room temperature. The UV-Vis results confirm directly the gold nano particles formation. The XRD and N2 adsorption results showed the formation of gold nano particles in the pores of montmorillonite with an average size of 5 nm obtained on samples with 2%Au-mont. The gold particles size increased with the increase of gold loading percentage. The reduction reaction of 4-nitrophenol into 4-aminophenol with NaBH4 catalyzed by Au-Na-montmorillonite catalyst exhibits remarkably a high activity; the reaction was completed within 9 min for 1Au-mont and within 3 min for 2Au-mont.

Keywords: Gold, montmorillonite, chemical reduction, nano particles

Procedia PDF Downloads 155