3 Interfacial Layer Effect on Novel p-Ni1-xO:Li/n-Si Heterojunction Solar Cells

Authors: Feng-Hao Hsu, Na-Fu Wang, Yu-Zen Tsai, Yu-Song Cheng, Cheng-Fu Yang, Mau-Phon Houng

Abstract:

This study fabricates p-type Ni1xO:Li/n-Si heterojunction solar cells (P+/n HJSCs) by using radio frequency (RF) magnetron sputtering and investigates the effect of substrate temperature on photovoltaic cell properties. Grazing incidence x-ray diffraction, four point probe, and ultraviolet-visible-near infrared discover the optoelectrical properties of p-Ni1-xO thin films. The results show that p-Ni1-xO thin films deposited at 300 oC has the highest grain size (22.4 nm), average visible transmittance (~42%), and electrical resistivity (2.7 Ωcm). However, the conversion efficiency of cell is shown only 2.33% which is lower than the cell (3.39%) fabricated at room temperature. This result can be mainly attributed to interfacial layer thickness (SiOx) reduces from 2.35 nm to 1.70 nm, as verified by high-resolution transmission electron microscopy.

Keywords: Solar Cells, sputtering, heterojunction, nickel oxide

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1478
2 Deposition of Transparent IGZO Conducting Thin Films by Co-Sputtering of Zn2Ga2O3 and In2O3 Targets at Room Temperature

Authors: Cheng-Fu Yang, Yu-Hsin Chen, Yuan-Tai Hsieh, Cheng-Shong Hong, Chia-Ching Wu, Yu-Jhen Liou

Abstract:

In this study, we investigated (In,Ga,Zn)Ox (IGZO) thin films and examined their characteristics of using Ga2O3-2 ZnO (GZO) co-sputtered In2O3 prepared by dual target radio frequency magnetron sputtering at room temperature in a pure Ar atmosphere. RF powers of 80 W and 70 W were used for GZO and pure In2O3, room temperature (RT) was used as deposition temperature, and the deposition time was changed from 15 min to 60 min. Structural, surface, electrical, and optical properties of IGZO thin films were investigated as a function of deposition time. Furthermore, the GZO co-sputtered In2O3 thin films showed a very smooth and featureless surface and an amorphous structure regardless of the deposition time due to the room temperature sputtering process. We would show that the co-sputtered IGZO thin films exhibited transparent electrode properties with high transmittance ratio and low resistivity.

Keywords: In2O3, IGZO, co-sputter, Ga2O3-2 ZnO

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2737
1 Using Printing Method and Post Heat Treatment to Fabricate CIS Absorber Layer

Authors: Yen-Lin Chen, Cheng-Fu Yang, Mao-An Chen, Chien-Chen Diao, Chia-Cheng Huang, Chin-Guo Kuo

Abstract:

In this study, the Mo-electrode thin films were deposited using two-stepped process and the high purity copper indium selenide-based powder (CuInSe2, CIS) was fabricated by using hydrothermal process by Nanowin Technology Co. Ltd. Because the CIS powder was aggregated into microscale particles, the CIS power was ground into nano-scale particles. 6 wt% CIS particles were mixed and dispersed into isopropyl alcohol (IPA). A new non-vacuum thin-film deposition process, spray coating method (SPM), was investigated to deposit the high-densified CIS absorber layers. 0.1 ml CIS solution was sprayed on the 20 mm×10 mm Mo/glass substrates and then the CuInSe2 thin films were annealed in a selenization furnace using N2 as atmosphere. The annealing temperature and time were set at 550oC and 5 min, and 0.0g~0.6g extra Se content was added in the furnace. The influences of extra Se content on the densification, crystallization, resistivity (ρ), hall mobility (μ), and carrier concentration of the CIS absorber layers were well investigated in this study.

Keywords: annealing, isopropyl alcohol, CuInSe2, spray coating method, selenization process

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1768

Abstracts

1 High-Frequency Modulation of Light-Emitting Diodes for New Ultraviolet Communications

Authors: Cheng-Fu Yang, Mau-Phon Houng, Cheng-Shong Hong, Jyun-Hao Liao, Meng-Chyi Wu, Bonn Lin, Chein-Ju Chen, Yu-Cheng Jhuang, Fang-Hsing Wang, Min-Chu Liu

Abstract:

Since the use of wireless communications has become critical nowadays, the available RF spectrum has become limited. Ultraviolet (UV) communication system can alleviate the spectrum constraint making UV communication system a potential alternative to future communication demands. Also, UV links can provide faster communication rate and can be used in combination with existing RF communication links, providing new communications diversity with higher user capacity. The UV region of electromagnetic spectrum has been of interest to detector, imaging and communication technologies because the stratospheric ozone layer effectively absorbs some solar UV radiation from reaching the earth surface. The wavebands where most of UV radiation is absorbed by the ozone are commonly known as the solar blind region. By operating in UV-C band (200-280 nm) the communication system can minimize the transmission power consumption since it will have less radiation noise. UV communication uses the UV ray as the medium. Electric signal is carried on this band after being modulated and then be transmitted within the atmosphere as channel. Though the background noise of UV-C communication is very low owing to the solar-blind feature, it leads to a large propagation loss. The 370 nm UV provides a much lower propagation loss than that the UV-C does and the recent device technology for UV source on this band is more mature. The fabricated 370 nm AlGaN light-emitting diodes (LEDs) with an aperture size of 45 m exhibit a modulation bandwidth of 165 MHz at 30 mA and a high power of 7 W/cm2 at 230 A/cm2. In order to solve the problem of low power in single UV LED, a UV LED array is presented in.

Keywords: ultraviolet (UV) communication, light-emitting diodes (LEDs), modulation bandwidth, LED array

Procedia PDF Downloads 204