2 The Effect of Yb3+ Concentration on Spectroscopic properties of Strontium Cerate Doped with Tm3+ and Yb3+

Authors: Haeyoung Choi, Yeon Woo Seo, Jung Hyun Jeong

Abstract:

Recently, the UC phosphors have attracted much attention owing to their wide applicability in areas such as biological fluorescence labeling, three-dimensional color displays, temperature sensor, solar cells, white light emitting diodes (WLEDs), fiber optic communication, anti-counterfeiting and other areas. The UC efficiency is mainly dependent on the host lattice and the interaction between the host lattice and doped ions. Up to date, various host matrices, such as oxides, fluorides, vanadates and phosphates, have been investigated as efficient UC luminescent hosts. Recently, oxide materials with low phonon energy have been investigated as the host matrices of UC materials due to their high chemical durability and physical stability. A series of Sr2CeO4: Tm3+/Yb3+ phosphors with different concentrations of Yb3+ ions have been successfully prepared using the high-energy ball milling method. In this study, we reported the UC luminescent properties of Tm3+/Yb3+ ions co-doped Sr2CeO4 phosphors under an excitation wavelength of 975 nm. Furthermore, the structural and morphological characteristics, as well as the UC luminescence mechanism were investigated in detail. The X-ray diffraction patterns confirmed their orthorhombic structure. Under 975 nm excitation, the emission peaks were observed at 478 nm (blue) and 652 nm (red), corresponding to the 1G4 → 3H6 and 1G4 → 3F4 transitions of Tm3+, respectively. The optimized doping concentration of Yb3+ ion was 10 mol%.

Keywords: Luminescence, Strontium Cerate, up-conversion, Tm3+, Yb3+

Procedia PDF Downloads 127
1 Influence of Sintering Temperatures in Er³⁺/Yb³⁺/Tm³⁺ Tri-Doped Y₂O₃ Nanophosphors

Authors: Hyeon Mi Noh, Ju Hyun Oh, Jung Hyun Jeong, Haeyoung Choi, Jung Hwan Kim

Abstract:

The Er³⁺/Yb³⁺/Tm³⁺ tri-doped Y₂O₃ nanophosphors were synthesized by solvothermal method and its temperature dependence of the white upconversion emission has been studied by using 975 nm laser diode. The upconversion emission spectra in 1 mol% Er³⁺/5 mol% Yb³⁺/xTm³ tri-doped Y₂O₃ nanophosphors sintered at 1000 °C with x from 0 to 0.5 mol%. The blue emission intensity increase with Tm³⁺ concentration from 0 to 0.5 mol%, it is due to the 2F7/2→2F5/2 transition of Yb³⁺ around 10,000 cm-1 could easily reach the Tm³⁺ sates. The white light is composed with the blue (1G4→3H6 of Tm³⁺), green (2H11/2, 4S3/2→4I15/2 of Er³⁺), and red (4F9/2→4I15/2 of Er³⁺) upconversion radiations. The Y₂O₃: Er³⁺/Yb³⁺/Tm³⁺ nanophosphors show from white to green upconversion emission at power of 600 mW/cm² as sintering temperature increased. The calculated Commission Internationale de l’Eclairage (CIE) coordinates can be located in the white area with various sintering temperatures, in sintered at 1000 °C, and their color coordinates are very close to the standard white-light emission (0.33, 0.33). Their upconversion processes were explained by measuring the upconversion luminescence spectra and pump power dependence and energy level diagram.

Keywords: Energy transfer, nanophosphors, solvothermal method, white upconversion emission

Procedia PDF Downloads 142