1 Laser Beam Forming of 3 mm Steel Plate and the Evolving Properties

Authors: Esther Akinlabi, Mukul Shukla, Stephen Akinlabi, Marwala Tshilidzi

Abstract:

This paper reports the evolving properties of a 3 mm low carbon steel plate after Laser Beam Forming achieve this objective, the chemical analyse material and the formed components were carried thereafter both were characterized through microhardness profiling microstructural evaluation and tensile testing. showed an increase in the elemental concentration of the component when compared to the as received attributed to the enhancement property of the LBF process Ultimate Tensile Strength (UTS) and the Vickers the formed component shows an increase when compared to the as received material, this was attributed to strain hardening and grain refinement brought about by the LBF process. The microstructure of the as received steel consists of equiaxed ferrit that of the formed component exhibits elongated orming process (LBF). To es of the as received out and compared; profiling, The chemical analyses formed material; this can be process. The microhardness of ferrite and pearlite while grains.

Keywords: deformation, Laser beam forming, elongated grains

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1582

Abstracts

3 Effect of Welding Current on Mechanical Properties and Microstructure of Tungsten Inert Gas Welding of Type-304 Austenite Stainless Steel

Authors: Esther Akinlabi, Emmanuel Ogundimu, Mutiu Erinosho

Abstract:

The aim of this paper is to study the effect of welding current on the microstructure and the mechanical properties. Material characterizations were conducted on a 6 mm thick plates of type-304 austenite stainless steel, welded by TIG welding process at two different welding currents of 150 A (Sample F3) and 170 A (Sample F4). The tensile strength and the elongation obtained from sample F4 weld were approximately 584 MPa and 19.3 %; which were higher than sample F3 weld. The average microhardness value of sample F4 weld was found to be 235.7 HV, while that of sample F3 weld was 233.4 HV respectively. Homogenous distribution of iron (Fe), chromium (Cr) and nickel (Ni) were observed at the welded joint of the two samples. The energy dispersive spectroscopy (EDS) analysis revealed that Fe, Cr, and Ni made up the composition formed in the weld zone. The optimum welding current of 170 A for TIG welding of type-304 austenite stainless steel can be recommended for high-tech industrial applications.

Keywords: Process, Microstructure, Microhardness, tensile, MIG welding, shear stress TIG welding, TIG-MIG welding

Procedia PDF Downloads 23
2 Operational Advantages of Tungsten Inert Gas over Metal Inert Gas Welding Process

Authors: Esther Akinlabi, Emmanuel Ogundimu, Mutiu Erinosho

Abstract:

In this research, studies were done on the material characterization of type 304 austenitic stainless steel weld produced by TIG (Tungsten Inert Gas) and MIG (Metal Inert Gas) welding processes. This research is aimed to establish optimized process parameters that will result in a defect-free weld joint, homogenous distribution of the iron (Fe), chromium (Cr) and nickel (Ni) was observed at the welded joint of all the six samples. The welded sample produced at the current of 170 A by TIG welding process had the highest ultimate tensile strength (UTS) value of 621 MPa at the welds zone, and the welded sample produced by MIG process at the welding current of 150 A had the lowest UTS value of 568 MPa. However, it was established that TIG welding process is more appropriate for the welding of type 304 austenitic stainless steel compared to the MIG welding process.

Keywords: Process, Microstructure, Microhardness, tensile, MIG welding, shear stress TIG welding, TIG-MIG welding

Procedia PDF Downloads 31
1 An Experimental Study on the Effect of Heat Input on the Weld Efficiency of TIG-MIG Hybrid Welding of Type-304 Austenitic Stainless Steel

Authors: Esther Akinlabi, Emmanuel Ogundimu, Mutiu Erinosho

Abstract:

Welding is described as the process of joining metals so that bonding can be created as a result of inter-atomic penetration. This study investigated the influence of heat input on the efficiency of the welded joints of 304 stainless steel. Three welds joint were made from two similar 304 stainless steel plates of thickness 6 mm. The tensile results obtained showed that the maximum average tensile strength of 672 MPa is possessed by the sample A1 with low heat input. It was discovered that the tensile strength, % elongation and weld joint efficiency decreased with the increase in heat input into the weld. The average % elongation for the entire samples ranged from 28.4% to 36.5%. Sample A1 had the highest joint efficiency of 94.5%. However, the optimum welding current of 190 for TIG- MIG hybrid welding of type-304 austenite stainless steel can be recommended for advanced technological applications such as aircraft manufacturing, nuclear industry, automobile industry, and processing industry.

Keywords: Process, Microstructure, Microhardness, tensile, MIG welding, shear stress TIG welding, TIG-MIG welding

Procedia PDF Downloads 19