2 Functionalized PU Foam for Water Filtration

Authors: Nidal H. Abu-Zahra, Subhashini Gunashekar

Abstract:

Polyurethane foam is functionalized with Sulfonic acid groups to remove lead ions (Pb2+) from drinking water through a cation exchange process. The synthesis is based on addition polymerization of the -NCO groups of an isocyanate with the –OH groups of a polyol to form the urethane. Toluene-diisocyanateis reacted with Polypropylene glycol to form a linear pre-polymer, which is further polymerized using a chain extender, N, N-bis(2-hydorxyethyl)-2-aminoethane-sulfonic acid (BES). BES acts as a functional group site to exchange Pb2+ ions. A set of experiments was designed to study the effect of various processing parameters on the performance of the synthesized foam. The maximum Pb2+ ion exchange capacity of the foam was found to be 47ppb/g from a 100ppb Pb2+ solution over a period of 60 minutes. A multistage batch filtration process increased the lead removal to 50-54ppb/3g of foam over a period of 90 minutes.

Keywords: Adsorption, functionalized, ion exchange, polyurethane, sulfonic

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2721
1 Low Temperature Ethanol Gas Sensor based on SnO2/MWNTs Nanocomposite

Authors: O. Alizadeh Sahraei, A. Khodadadi, Y. Mortazavi, M. Vesali Naseh, S. Mosadegh

Abstract:

A composite made of plasma functionalized multiwall carbon nanotubes (MWNTs) coated with SnO2 was synthesized by sonochemical precipitation method. Thick layer of this nanocomposite material was used as ethanol sensor at low temperatures. The composite sensitivity for ethanol has increased by a factor of 2 at room temperature and by a factor of 13 at 250°C in comparison to that of pure SnO2. SEM image of nanocomposite material showed MWNTs were embedded in SnO2 matrix and also a higher surface area was observed in the presence of functionalized MWNTs. Greatly improved sensitivity of the composite material to ethanol can be attributed to new gas accessing passes through MWNTs and higher specific surface area.

Keywords: nanocomposite, Carbon Nanotube, Gas Sensor, functionalized, tin oxide, Low temperature