2 Thermal Stability and Crystallization Behaviour of Modified ABS/PP Nanocomposites

Authors: Marianna I. Triantou, Petroula A. Tarantili

Abstract:

In this research work, poly (acrylonitrile-butadienestyrene)/ polypropylene (ABS/PP) blends were processed by melt compounding in a twin-screw extruder. Upgrading of the thermal characteristics of the obtained materials was attempted by the incorporation of organically modified montmorillonite (OMMT), as well as, by the addition of two types of compatibilizers; polypropylene grafted with maleic anhydride (PP-g-MAH) and ABS grafted with maleic anhydride (ABS-g-MAH). The effect of the above treatments was investigated separately and in combination. Increasing the PP content in ABS matrix seems to increase the thermal stability of their blend and the glass transition temperature (Tg) of SAN phase of ABS. From the other part, the addition of ABS to PP promotes the formation of its β-phase, which is maximum at 30 wt% ABS concentration, and increases the crystallization temperature (Tc) of PP. In addition, it increases the crystallization rate of PP.The β-phase of PP in ABS/PP blends is reduced by the addition of compatibilizers or/and organoclay reinforcement. The incorporation of compatibilizers increases the thermal stability of PP and reduces its melting (ΔΗm) and crystallization (ΔΗc) enthalpies. Furthermore it decreases slightly the Tgs of PP and SAN phases of ABS/PP blends. Regarding the storage modulus of the ABS/PP blends, it presents a change in their behavior at about 10°C and return to their initial behavior at ~110°C. The incorporation of OMMT to no compatibilized and compatibilized ABS/PP blends enhances their storage modulus.

Keywords: Polypropylene, compatibilizer, acrylonitrile, butadiene, styrene terpolymer, organoclay

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2476
1 Preparation of Polylactic Acid Graft Polyvinyl Acetate Compatibilizers for 50/50 Starch/PLLA Blending

Authors: S. Buchatip, A. Petchsuk

Abstract:

Polylactic acid-g-polyvinyl acetate (PLLA-g-PVAc) was used as a compatibilizer for 50/50 starch/PLLA blend. PLLA-g- PVAc with different mol% of PVAc contents were prepared by grafting PVAc onto PLLA backbone via free radical polymerization in solution process. Various conditions such as type and the amount of initiator, monomer concentration, polymerization time and temperature were studied. Results showed that the highest mol% of PVAc grafting (16 mol%) was achieved by conducting graft copolymerization in toluene at 110°C for 10 h using DCP as an initiator. Chemical structure of the PVAc grafted PLLA was confirmed by 1H NMR. Blending of modified starch and PLLA in the presence compatibilizer with different amounts and mol% PVAc was acquired using internal mixer at 160°C for 15 min. Effects of PVAc content and the amount of compatibilizer on mechanical properties of polymer blend were studied. Results revealed that tensile strength and tensile modulus of polymer blend with higher PVAc grafting content compatibilizer showed better properties than that of lower PVAc grafting content compatibilizer. The amount of compatibilizer was found optimized in the range of 0.5-1.0 Wt% depending on the mol% PVAc.

Keywords: Starch, compatibilizer, blending, PLLA, free radical polymerization