3 Statistical Analysis of Failure Cases in Aerospace

Authors: J. H. Lv, W. Z. Wang, S.W. Liu

Abstract:

The major concern in the aviation industry is the flight safety. Although great effort has been put onto the development of material and system reliability, the failure cases of fatal accidents still occur nowadays. Due to the complexity of the aviation system, and the interaction among the failure components, the failure analysis of the related equipment is a little difficult. This study focuses on surveying the failure cases in aviation, which are extracted from failure analysis journals, including Engineering Failure Analysis and Case studies in Engineering Failure Analysis, in order to obtain the failure sensitive factors or failure sensitive parts. The analytical results show that, among the failure cases, fatigue failure is the largest in number of occurrence. The most failed components are the disk, blade, landing gear, bearing, and fastener. The frequently failed materials consist of steel, aluminum alloy, superalloy, and titanium alloy. Therefore, in order to assure the safety in aviation, more attention should be paid to the fatigue failures.

Keywords: Aviation industry, failure analysis, failure component, fatigue.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 494
2 Failure Cases Analysis in Petrochemical Industry

Authors: S. W. Liu, J. H. Lv, W. Z. Wang

Abstract:

In recent years, the failure accidents in petrochemical industry have been frequent, and have posed great security problems in personnel and property. The improvement of petrochemical safety is highly requested in order to prevent re-occurrence of severe accident. This study focuses on surveying the failure cases occurred in petrochemical field, which were extracted from journals of engineering failure, including engineering failure analysis and case studies in engineering failure analysis. The relation of failure mode, failure mechanism, type of components, and type of materials was analyzed in this study. And the analytical results showed that failures occurred more frequently in vessels and piping among the petrochemical equipment. Moreover, equipment made of carbon steel and stainless steel accounts for the majority of failures compared to other materials. This may be related to the application of the equipment and the performance of the material. In addition, corrosion failures were the largest in number of occurrence in the failure of petrochemical equipment, in which stress corrosion cracking accounts for a large proportion. This may have a lot to do with the service environment of the petrochemical equipment. Therefore, it can be concluded that the corrosion prevention of petrochemical equipment is particularly important.

Keywords: Cases analysis, corrosion, failure, petrochemical industry.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 554
1 Raman Scattering and PL Studies on AlGaN/GaN HEMT Layers on 200 mm Si(111)

Authors: W. Z. Wang, S. Todd, S. B. Dolmanan, K. B. Lee, L. Yuan, H. F. Sun, S. L. Selvaraj, M.Krishnakumar, G. Q. Lo, S. Tripathy

Abstract:

The crystalline quality of the AlGaN/GaN high electron mobility transistor (HEMT) structure grown on a 200 mm silicon substrate has been investigated using UV-visible micro- Raman scattering and photoluminescence (PL). The visible Raman scattering probes the whole nitride stack with the Si substrate and shows the presence of a small component of residual in-plane stress in the thick GaN buffer resulting from a wafer bowing, while the UV micro-Raman indicates a tensile interfacial stress induced at the top GaN/AlGaN/AlN layers. PL shows a good crystal quality GaN channel where the yellow band intensity is very low compared to that of the near-band-edge transition. The uniformity of this sample is shown by measurements from several points across the epiwafer.

Keywords: Raman, photo luminescence, AlGaN/GaN, HEMT.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 3489