3 Aging Effect on Mechanical Behavior of Duplex Satinless Steel

Authors: Jungho Moon, Tae Kwon Ha

Abstract:

Effect of alloying on the microstructure and mechanical properties of heat-resisting duplex stainless steel (DSS) for Mg production was investigated in this study. 25Cr-8Ni based DSS’s were cast into rectangular ingots of which the dimension was 350×350×100 mm3 . Nitrogen and Yttrium were added in the range within 0.3 in weight percent. Phase equilibrium was calculated using the FactSage®, thermodynamic software. Hot exposure, high temperature tensile and compression tests were conducted on the ingots at 1230oC, which is operation temperature employed for Mg production by Silico-thermic reduction. The steel with N and Y showed much higher strength than 310S alloy in both tensile and compression tests. By thermal exposition at 1230oC for 200 hrs, hardness of DSS containing N and Y was found to increase. Hot workability of the heat-resisting DSS was evaluated by employing hot rolling at 1230 oC. Hot shortness was observed in the ingot with N and found to disappear after addition of Y.

Keywords: Microstructure, duplex stainless steel, alloying elements, eutectic carbides, aging treatment

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1127
2 Alloying Effect on Hot Workability of M42 High Speed Steel

Authors: Tae Kwon Ha, Jung-Ho Moon

Abstract:

In the present study, the effect of Si, Al, Ti, Zr, and Nb addition on the microstructure and hot workability of cast M42 tool steels, basically consisting of 1.0C, 0.2Mn, 3.8Cr, 1.5W, 8.5Co, 9.2Mo, and 1.0V in weight percent has been investigated. Tool steels containing Si of 0.25 and 0.5wt.%, Al of 0.06 and 0.12wt.%, Ti of 0.3wt.%, Zr of 0.3wt.%, and Nb of 0.3wt.% were cast into ingots of 140mm ´ 140mm ´ 330mm by vacuum induction melting. After solution treatment at 1150oC for 1.5hr followed by furnace cooling, hot rolling at 1180oC was conducted on the ingots. Addition of titanium, zirconium and niobium was found to retard the decomposition of the eutectic carbides and result in the deterioration of hot workability of the tool steels, while addition of aluminum and silicon showed relatively well decomposed carbide structure and resulted in sound hot rolled plates.

Keywords: Microstructure, high speed steels, alloying elements, eutectic carbides, hot workability

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2255
1 Evaluation of Alloying Additions on the Microstructure and IMC Formation of Sn-Ag-Cu Solder on Cu and Ni (P) Substrates

Authors: S.O. Shazlin, M.S. Nurulakmal

Abstract:

Studies have shown that the SnAgCu solder family has been widely used as a replacement for conventional Sn-Pb solders. An attractive approach is by introducing alloying additives (rare earth elements (RE), Zn, Co, Fe, Ni, Sb) into the SnAgCu solder, which helps in refining the microstructure also improving the mechanical and wetting properties of the solder. The present work focuses on the effect of additions of 0.5% Ce and Fe into Sn-3.0Ag-0.5Cu solder, in attempt to reduce the intermetallic compound (IMC) growth and reflow properties of the solder on Cu and Ni (P) surface finish, as well as effects thermal aging on the formation of intermetallic compound (IMC) on different surface finish. Excessive intermetallic compound growth may effect the interface and solder joint due to the brittle nature of the intermetallic compounds. Thus, by introducing alloying elements, IMC layer thickness can be decrease, resulting in better joint and solder reliability.

Keywords: alloying elements, reflow, thermal aging, Cu and Ni (P) Substrate, Intermetallic Compound (IMC)

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1327