Search results for: Vitoldas Vaitkevičius

Authors: Vitoldas Vaitkevičius, Evaldas Šerelis

Abstract:

Silica fume, also known as microsilica (MS) or condensed silica fume is a by-product of the production of silicon metal or ferrosilicon alloys. Silica fume is one of the most effective pozzolanic additives which could be used for ultrahigh performance and other types of concrete. Despite the fact, however is not entirely clear, which amount of silica fume is most optimal for UHPC. Main objective of this experiment was to find optimal amount of silica fume for UHPC with and without thermal treatment, when different amount of quartz powder is substituted by silica fume. In this work were investigated four different composition of UHPC with different amount of silica fume. Silica fume were added 0, 10, 15 and 20% of cement (by weight) to UHPC mixture. Optimal amount of silica fume was determined by slump, viscosity, qualitative and quantitative XRD analysis and compression strength tests methods.

Keywords: compressive strength, silica fume, ultrahigh performance concrete, XRD

Procedia PDF Downloads 264

Authors: Vitoldas Vidikas, Algirdas Augonis

Abstract:

Different ecological binders have been used to minimize the negative effects of cement production and use on the environment. Wood ash is one of these alternative binders, and there has been increasing research related to this topic recently. The incineration process in power plants produces numerous amounts of residues, the potential applications of which remain incompletely understood. However, it is established that wood ash improves concrete properties, serves as a fertilizer, and substitutes natural aggregates in artificial aggregate production. This study presents the production and properties of wood ash artificial aggregate, their integration into concrete, and the assessment of their strength. Due to the aforementioned large amount of incineration waste accumulating in landfills, the recovery of this waste is important, and reuse and recycling of this waste is necessary. Artificial aggregates stand out as a significant innovation in this effort. In this study, the artificial aggregate was carbonized using wood waste incineration ash and alkali activators, with the alkaline activator consisting of Ca(OH)2. Various mixtures were formulated, incorporating different materials and compositions of activators. Initially, fillers were created using wood ash, followed by formulations subsequently supplemented with wood ash. A series of tests, including XRD, SEM, and compression tests, were conducted. The artificial aggregate exhibits minimal water absorption and holds potential as a substitute for natural materials. Its prospective applications extend to agriculture, where it could function as a fertilizer, and construction, where it could serve as an artificial aggregate. Concrete incorporating the artificial aggregate demonstrates stability, stiffness, and relatively low density. In our research, a test was developed and applied to determine the compressive strength of a manufactured artificial aggregate, not by direct loading, but by subjecting a cementitious test specimen containing the aggregate under test to a load. In this way, the test not only determines the effect of the aggregate on the compressive behavior of such a specimen but also the characteristics of the fracture, which shows how these artificial aggregates adhere to the cement matrix. This testing methodology holds promise for evaluating the suitability of artificial aggregates in construction materials, not only in terms of their load-bearing capacity but also of their adhesion to the mineral binder. The results showed that the mechanical properties of granular artificial aggregates vary significantly with the amount of binder (lime), i.e. an increase of ~15% in the amount of binder resulted in an increase in the crushing strength of the carbonized aggregate by ~15-20%, while the compressive strength of the cementitious specimen with this aggregate increased by ~18%.

Keywords: wood ash, artificial aggregate, carbonization, compressive strength

Procedia PDF Downloads 4

Authors: Augustas Vaitkevicius, Mikhail Korjik, Eugene Tretyak, Ekaterina Trusova, Gintautas Tamulaitis

Abstract:

Silicate materials are widely used as luminescent materials in amorphous and crystalline phase. Lithium silicate glass is popular for making neutron sensitive scintillation glasses. Cerium-doped single crystalline silicates of rare earth elements and yttrium have been demonstrated to be good scintillation materials. Due to their high thermal and photo-stability, silicate glass ceramics are supposed to be suitable materials for producing light converters for high power white light emitting diodes. In this report, the influence of glass composition and crystallization on photoluminescence (PL) of different silicate glasses was studied. Barium (BaO-2SiO₂) and lithium (Li₂O-2SiO₂) glasses were under study. Cerium, dysprosium, erbium and europium ions as well as their combinations were used for doping. The influence of crystallization was studied after transforming the doped glasses into glass ceramics by heat treatment in the temperature range of 550-850 degrees Celsius for 1 hour. The study was carried out by comparing the photoluminescence (PL) spectra, spatial distributions of PL parameters and quantum efficiency in the samples under study. The PL spectra and spatial distributions of their parameters were obtained by using confocal PL microscopy. A WITec Alpha300 S confocal microscope coupled with an air cooled CCD camera was used. A CW laser diode emitting at 405 nm was exploited for excitation. The spatial resolution was in sub-micrometer domain in plane and ~1 micrometer perpendicularly to the sample surface. An integrating sphere with a xenon lamp coupled with a monochromator was used to measure the external quantum efficiency. All measurements were performed at room temperature. Chromatic properties of the light emission from the glasses and glass ceramics have been evaluated. We observed that the quantum efficiency of the glass ceramics is higher than that of the corresponding glass. The investigation of spatial distributions of PL parameters revealed that heat treatment of the glasses leads to a decrease in sample homogeneity. In the case of BaO-2SiO₂: Eu, 10 micrometer long needle-like objects are formed, when transforming the glass into glass ceramics. The comparison of PL spectra from within and outside the needle-like structure reveals that the ratio between intensities of PL bands associated with Eu²⁺ and Eu³⁺ ions is larger in the bright needle-like structures. This indicates a higher degree of crystallinity in the needle-like objects. We observed that the spectral positions of the PL bands are the same in the background and the needle-like areas, indicating that heat treatment imposes no significant change to the valence state of the europium ions. The evaluation of chromatic properties confirms applicability of the glasses under study for fabrication of white light sources with high thermal stability. The ability to combine barium and lithium glass matrixes and doping by Eu, Ce, Dy, and Tb enables optimization of chromatic properties.

Keywords: glass ceramics, luminescence, phosphor, silicate

Procedia PDF Downloads 277