Authors: Diana Serbezeanu, Ionela-Daniela Carja, Tachita Vlad-Bubulac, Sergiu Sova

Abstract:

New phosphorus-containing monomers having methoxy end functional groups were prepared from methyl 4-hydroxybenzoate and two different dichlorides with phosphorus, namely phenyl phosphonic dichloride and phenyl dichlorophosphate. The structures of the monomers were confirmed by FTIR and NMR spectroscopy. The assignments for the 1H, 13C and 31P chemical shifts are based on 1D and 2D NMR homo- and heteronuclear correlations (H,H-COSY (Correlation Spectroscopy), H,C-HMQC (Heteronuclear Multiple Quantum Correlation and H,C-HMBC (Heteronuclear Multiple Bond Correlation)) and 31P-13C couplings. The monomers exhibited good solubility in common organic solvents. Dimethyl sulfoxide was to be a good solvent to grow crystals of considerable size which were investigated by X-ray analysis. One of these two new monomers presented thermotropic liquid crystalline behaviour, as revealed by differential scanning calorimetry (DSC), polarized light microscopy (PLM) and X-ray diffraction (XRD). The transition temperature from crystal to liquid crystalline state (K→LC) was 143°C and from the LC to isotropic state (LC→I) was 167°C. Upon heating, bis(4-(methoxycarbonyl)phenyl formed fine textures, difficult to be ascribed to smectic or nematic phases. Upon cooling from the isotropic state, bis(4-(methoxycarbonyl)phenyl exhibited a mosaic-type texture. X-ray diffraction measurements at small angles (SAXS) of bis(4-(methoxycarbonyl)phenyl showed two peaks at 1.8 Å and 3.5 Å, respectively suggesting organization at supramolecular level.

Keywords: phosphorus-containing monomers, polarized light microscopy, structure investigation, thermotropic liquid crystalline properties

Procedia PDF Downloads 274

Authors: Tachita Vlad-Bubulac, Ionela-Daniela Carja, Diana Serbezeanu, Corneliu Hamciuc, Vicente Javier Forrat Perez

Abstract:

The present work describes the preparation of new organophosphorus compounds with high content of phosphorus followed by the incorporation of these compounds into epoxy resin systems in order to investigate the phosphorus effect in terms of thermal stability, flame-retardant and mechanical properties of modified epoxy resins. Thus, two new organophosphorus compounds have been synthesized and fully characterized. 6-Oxido-6H-dibenz[c,e][1,2]oxaphosphorinyl-phenylcarbinol has been prepared by the addition reaction of P–H group of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide to carbonyl group of benzaldehyde. By treating the phenylcarbinol derivative with POCl3 a new phosphorus compound was obtained, having a content of 12.227% P. The organophosphorus compounds have been purified by recrystallization while their chemical structures have been confirmed by melting point measurements, FTIR and HNMR spectroscopies. In the next step various flame-retardant epoxy resins with different content of phosphorus have been prepared starting from a commercial epoxy resin and using dicyandiamide (DICY) as a latent curing agent in the presence of an accelerator. Differential scanning calorimetry (DSC) has been applied to investigate the behavior and kinetics of curing process of thermosetting systems. The results showed that the best curing characteristic and glass transition temperature are obtained at a ratio of epoxy resin: DICY: accelerator equal to 94:5:1. The thermal stability of the phosphorus-containing epoxy resins was investigated by thermogravimetric analysis in nitrogen and air, DSC, SEM and LOI test measurements.

Keywords: epoxy resins, flame retardant properties, phosphorus-containing compounds, thermal stability

Procedia PDF Downloads 274

Authors: Ionela-Daniela Carja, Diana Serbezeanu, Tachita Vlad-Bubulac, Corneliu Hamciuc

Abstract:

Nowadays, epoxy materials are extensively used in ever more areas and under ever more demanding environmental conditions due to their remarkable combination of properties, light weight and ease of processing. However, these materials greatly increase the fire risk due to their flammability and possible release of toxic by-products as a result of their chemical composition which consists mainly from carbon and hydrogen atoms. Therefore, improving the fire retardant behaviour to prevent the loss of life and property is of particular concern among government regulatory bodies, consumers and manufacturers alike. Modification of epoxy resins with organophosphorus compounds, as reactive flame retardants or additives, is the key to achieving non-flammable advanced epoxy materials. Herein, a detailed characterization of fire behaviour for a series of phosphorus-containing epoxy thermosets is reported. A carefully designed phosphorus flame retardant additive was simply blended with a bifunctional bisphenol-A based epoxy resin. Further thermal cross-linking in the presence of various aminic hardeners led to eco-friendly flame retardant epoxy resins. The type of hardener, concentration of flame retardant additive, compatibility between the components of the mixture, char formation and morphology, thermal stability, flame retardant mechanisms were investigated. It was found that even a very low content of phosphorus introduced into the epoxy matrix increased the limiting oxygen index value to about 30%. In addition, the peak of the heat release rate value decreased up to 45% as compared to the one of the neat epoxy system. The main flame retardant mechanism was the condensed-phase one as revealed by SEM and XPS measurements.

Keywords: condensed-phase mechanism, eco-friendly phosphorus flame retardant, epoxy resin, thermal stability

Procedia PDF Downloads 267