Search results for: Sandip Bhattacharya

Authors: Souvik Das, Janak Lal, Arthita Dey, Goutam Mukhopadhyay, Sandip Bhattacharya

Abstract:

Telescopic Front Fork (TFF) used in two wheelers, mainly motorcycle, is made from high strength steel, and is manufactured by high frequency induction welding process wherein hot rolled and pickled coils are used as input raw material for rolling of hollow tubes followed by heat treatment, surface treatment, cold drawing, tempering, etc. The final application demands superior quality TFF tubes w.r.t. surface finish and dimensional tolerances. This paper presents the investigation of two different types of failure of fork during operation. The investigation consists of visual inspection, chemical analysis, characterization of microstructure, and energy dispersive spectroscopy. In this paper, comprehensive investigations of two failed tube samples were investigated. In case of Sample #1, the result revealed that there was a pre-existing crack, known as hook crack, which leads to the cracking of the tube. Metallographic examination exhibited that during field operation the pre-existing hook crack was surfaced out leading to crack in the pipe. In case of Sample #2, presence of internal oxidation with decarburised grains inside the material indicates origin of the defect from slab stage.

Keywords: telescopic front fork, induction welding, hook crack, internal oxidation

Procedia PDF Downloads 95

Authors: Subhadeep Mandal, Sujoy Bhattacharya, Pabitra Mitra, Diya Guha Roy, Seema Bhattacharya

Abstract:

E-commerce firms allow customers to evaluate and review the things they buy as a positive or bad experience. The e-commerce transaction processes are made up of a variety of diverse organizations and activities that operate independently but are connected together to complete the transaction (from placing an order to the goods reaching the client). After a negative shopping experience, clients frequently disregard the critical assessment of these businesses and submit their feedback on an all-over basis, which benefits certain enterprises but is tedious for others. In this article, we solely dealt with negative reviews and attempted to distinguish between negative reviews where the e-commerce firm is explicitly blamed by customers for a bad purchasing experience and other negative reviews.

Keywords: e-commerce, online shopping, customer reviews, customer behaviour, text analytics, n-grams classification

Procedia PDF Downloads 218

Authors: Souvik Das, Sandip Bhattacharya, Goutam Mukhopadhyay, Manashi Adhikary

Abstract:

Wires breakages during cold drawing are a complex phenomenon; wire breakages may be induced by improper wire-rod quality, inappropriate heat-treated microstructure, and/or lubrication breakdown on the wire surface. A comprehensive metallurgical investigation of failed/broken wire samples is therefore essential for understanding the origin of failure. Frequent breakage of wires during drawing is a matter of serious concern to the wire drawers as it erodes their already slim margins through reduced productivity and loss in yield. The present paper highlights the failure investigation of wires of Low Relaxation Prestressed High Carbon grade during cold drawing due to entrapment of hard constituents detached from the roller entry guide during rolling operations. The hardness measurement of this entrapped location indicates 54.9 Rockwell Hardness as against the rest portion 33.4 Rockwell Hardness. The microstructure chemical analysis and X-ray mapping analysis data of the entrapment location confirmed complex chromium carbide originated from D2-steel used in entry guide during the rolling process. Since the harder entrapped phase could not be deformed in the same manner as the parent phase, the failure of the wire rod occurs during hot rolling.

Keywords: LRPC, D2-steel, chromium carbide, roller guide

Procedia PDF Downloads 126

Authors: Urbi Pal, Piyas Palit, Jitendra Mathur, Abhay Chaturvedi, Sandip Bhattacharya

Abstract:

The hot rolled slab lifting crane cable reel drum (CRD) failed due to failure of cable reel flat spring which are inside the cassette of CRD. CRD is used for the movement of tong cable. Stereoscopic observation revealed beach marks and Scanning Electron Microscopy showed striations confirming fatigue mode of failure. Chemical composition should be spring steel (Cr-Mo-V) as per IS 3431:1982 instead of C-Mn steel. To find out the reason of fatigue failure, the theoretical fatigue life of flat spiral spring has been calculated. The calculation of number of fatigue cycles included bending moment, maximum stress on the spring, ultimate tensile strength and alternative stress. The bending moment determination has been taken account with various parameters like Young’s Modulus, width, thickness, outer diameter, arbor diameter, pay out the length and angular deflection in rotations. With all the required data, the calculated fatigue life turned to be 10000 cycles, but the spring served 15000 cycles which clearly indicated beyond fatigue life usage. Different UTS values have been plotted with respect to the number of fatigue cycles and clearly showed that the increase in UTS by 40% increases fatigue life by 50%. The significance of higher UTS lied here, and higher UTS depends on modified chemistry with proper tempered martensite microstructure. This kind of failure can be easily avoided by changing the crane spring maintenance schedule from 2 years to 1.5 years considering 600 cycles per month. The plant has changed changing the schedule of cable reel spring and procured new flat reel spring made of 50CrV2 steel.

Keywords: cable reel spring, fatigue life, stress, spring steel

Procedia PDF Downloads 114

Authors: S. S. Singh, A. Bhattacharya, S. Bhattacharya

Abstract:

The eukaryotic exosome complex plays a pivotal role in RNA biogenesis, maturation, surveillance and differential expression of various RNAs in response to varying environmental signals. The exosome is composed of evolutionary conserved nine core subunits and the associated exonucleases Rrp6 and Rrp44. Rrp6p is crucial for the processing of rRNAs, other non-coding RNAs, regulation of polyA tail length and termination of transcription. Rrp6p, a 3’-5’ exonuclease is required for degradation of 5’-external transcribed spacer (ETS) released from the rRNA precursors during the early steps of pre-rRNA processing. In the parasitic protist Entamoeba histolytica in response to growth stress, there occurs the accumulation of unprocessed pre-rRNA and 5’ ETS sub fragment. To understand the processes leading to this accumulation, we looked for Rrp6 and the exosome subunits in E. histolytica, by in silico approaches. Of the nine core exosomal subunits, seven had high percentage of sequence similarity with the yeast and human. The EhRrp6 homolog contained exoribonuclease and HRDC domains like yeast but its N- terminus lacked the PMC2NT domain. EhRrp6 complemented the temperature sensitive phenotype of yeast rrp6Δ cells suggesting conservation of biological activity. We showed 3’-5’ exoribonuclease activity of EhRrp6p with in vitro-synthesized appropriate RNAs substrates. Like the yeast enzyme, EhRrp6p degraded unstructured RNA, but could degrade the stem-loops slowly. Furthermore, immunolocalization revealed that EhRrp6 was nuclear-localized in normal cells but was diminished from nucleus during serum starvation, which could explain the accumulation of 5’ETS during stress. Our study shows functional conservation of EhRrp6p in E.histolytica, an early-branching eukaryote, and will help to understand the evolution of exosomal components and their regulatory function.

Keywords: entamoeba histolytica, exosome complex, rRNA processing, Rrp6

Procedia PDF Downloads 163

Authors: Sandip Mitra

Abstract:

Studies on Governance and Accountability has often stressed the need to release Data in public domain to increase transparency ,which otherwise act as an evidence of performance. However, inefficient handling, lack of capacity and the dynamics of transfers (especially fund transfers) are important issues which need appropriate attention. E-Governance alone can not serve as a measure of transparency as long as a comprehensive planning is instituted. Studies on Governance and public exposure has often triggered public opinion in favour or against any government. The root of the problem (especially in local governments) lies in the management of the governance. The participation of the people in the local government functioning, the networks within and outside the locality, synergy with various layers of Government are crucial in understanding the activities of any government. Unfortunately, data on such issues are not released in the public domain .If they are at all released , the extraction of information is often hindered for complicated designs. A Study has been undertaken with a few local Governments in India. The data has been analysed to substantiate the views.

Keywords: accountability, e-governance, transparency, local government

Procedia PDF Downloads 398

Authors: Sachin S. Patil, Mohan I. Mehta, Sandip J. Sutar, Akshay B. Patil, Shreyas S. Kirwai, Suresh Arangi

Abstract:

MnS is the most commonly found inclusion in steel, which is desirable for machinability of alloy steels but only up to a certain limit, beyond which it weakens fatigue properties of steel. In present work, the effect of sulfur content and its inclusions on the fatigue behavior of AISI 4140 steel is studied (sulfur content 0.002% and 0.016%). Metallurgical analysis, Mechanical testing and Rotating Bending Fatigue (RBF) test were carried out. With the increase in sulfur content, ductility and toughness of the material decrease significantly and large scatter is observed in UTS and impact energy values. From the results of RBF testing, it can be observed that increase in sulfur content from 0.002% to 0.016% has a negligible effect on the endurance strength of AISI 4140 for similar hardness level. Fractography analysis was carried out to study the failure modes in testing.

Keywords: AISI 4140, sulfur content, MnS inclusion, rotating bending fatigue

Procedia PDF Downloads 367

Authors: Atul K. Desai, Jigar K. Sevalia, Sandip A. Vasanwala

Abstract:

When a building is located in an urban area, it is exposed to a wind of different characteristics then wind over an open terrain. This is development of turbulent wake region behind an upstream building. The interaction with upstream building can produce significant changes in the response of the tall building. Here, in this paper, an attempt has been made to study wind induced interference effects on tall building. In order to study wind induced interference effect (IF) on Tall Building, initially a tall building (which is termed as Principal Building now on wards) with square plan shape has been considered with different Height to Width Ratio and total drag force is obtained considering different terrain conditions as well as different incident wind direction. Then total drag force on Principal Building is obtained by considering adjacent building which is termed as Interfering Building now on wards with different terrain conditions and incident wind angle. To execute study, Computational Fluid Dynamics (CFD) Code namely Fluent and Gambit have been used.

Keywords: computational fluid dynamics, tall building, turbulent, wake region, wind

Procedia PDF Downloads 497

Authors: Angana Bhattacharya, Rakesh Sarkar, Gagan Kumar

Abstract:

Toroidal resonances, a new class of electromagnetic excitations, demonstrate exceptional properties as compared to electric and magnetic dipolar resonances. The advantage of narrow linewidth in toroidal resonance is utilized in this proposed work, where a bilayer metamaterial (MM) sensor has been designed in the terahertz frequency regime (THz). A toroidal MM geometry in a single layer is first studied. A second identical MM geometry placed on top of the first layer results in the coupling of toroidal excitations, leading to an increase in the quality factor (Q) of the resonance. The sensing capability of the resonance is studied. Further, the dynamic switching from an 'off' stage to an 'on' stage in the bilayer configuration is explored. The ardent study of such toroidal bilayer MMs could provide significant potential in the development of bio-molecular and chemical sensors, switches, and modulators.

Keywords: toroidal resonance, bilayer, metamaterial, terahertz, sensing, switching

Procedia PDF Downloads 119

Authors: Pallab Bhattacharya, C. K. Das

Abstract:

Development of microwave absorbing material is a growing field of research in both the commercial and defense sector, and also to enrich the field of stealth technology. The recent work is attentive to the preparation of nanocomposite based on acid modified MWCNT, hexagonal shaped magnetic M-type hexaferrite (CuFe10Al2O19) and polyaniline. CuFe10Al2O19 was prepared by a facile chemical co-precipitation method. An in-situ approach was employed for the coating of polyaniline on MWCNT/CuFe10Al2O19 nanocomposite. The final fabrication of this nanocomposite for microwave measurements was done suitably in the matrix of thermoplastic polyurethane with 10% filler content. The nanocomposites showed the maximum reflection loss of -60.2 dB (in X-band) at the thickness of 2.5 mm with a broad absorption range in contrast to the pristine MWCNT and CuFe10Al2O19. Addition of PANI improves the microwave absorption property of the nanocomposites. The thermal stability of the prepared nanocomposites is also very high.

Keywords: magnetic materials, microwave absorption, MWCNT, nanocomposites

Procedia PDF Downloads 261

Authors: Kunj Parikh, S. Bhattacharya, V. Natarajan

Abstract:

TCAD numerical simulation is one of the most tried and tested powerful tools for designing devices in semiconductor foundries worldwide. It has also been used to explain conduction in organic thin films where the processing temperature is often enough to make homogeneous samples (often imperfect, but homogeneously imperfect). In this report, we have presented the results of TCAD simulation in multi-grain thin films. The work has addressed the inhomogeneity in one dimension, but can easily be extended to two and three dimensions. The effect of grain boundaries has mainly been approximated as barriers located at the junction between two adjacent grains. The effect of the value of grain boundary barrier, the bulk traps, and the measurement temperature have been investigated.

Keywords: polycrystalline thin films, space charge limited conduction, Technology Computer-Aided Design (TCAD) simulation, traps

Procedia PDF Downloads 173

Authors: Sunsoo Kim, Niladri Das, Raktim Bhattacharya

Abstract:

This paper addresses modeling and control of a six-degree-of-freedom unmanned aerial vehicle capable of vertical take-off and landing in the presence of wind disturbances. We design a hybrid vehicle that combines the benefits of both the fixed-wing and the rotary-wing UAVs. A non-linear model for the hybrid vehicle is rapidly built, combining rigid body dynamics, aerodynamics of wing, and dynamics of the motor and propeller. Further, we design a H₂ optimal controller to make the UAV robust to wind disturbances. We compare its results against that of proportional-integral-derivative and linear-quadratic regulator based control. Our proposed controller results in better performance in terms of root mean squared errors and time responses during two scenarios: hover and level- flight.

Keywords: hybrid UAVs, VTOL, aircraft modeling, H2 optimal control, wind disturbances

Procedia PDF Downloads 120

Authors: Sandip Sharma, Jayesh Ruparelia

Abstract:

The present work focuses on the comparative study of ozone based advanced oxidation processes (AOPs): O3, O3/UV and O3/UV/Persulfate for mineralization of synthetic wastewater containing Reactive Black5 (RB5) dye. The effect of various parameters: pH, ozone flow rate, initial concentration of dye and intensity of UV light was analyzed to access performance efficiency of AOPs. The performance of all the three AOPs was evaluated on the basis of decolorization, % TOC removal and ozone consumption. The highest mineralization rate of 86.83% was achieved for O3/UV/Persulfate followed by 71.53% and 66.82 % for O3/UV and O3 respectively. This is attributed to the fact that Persulfate ions (S2O82-) upon activation produce sulfate radical (SO4-●) which is very strong oxidant capable of degrading a wide variety of recalcitrant organic compounds, moreover to enhance the performance of Persulfate it is activated using UV irradiation. On increasing the intensity of UV irradiation from 11W to 66W, TOC removal efficiency is increased by 59.04%. Ozone based AOPs gives better mineralization on basic conditions, at pH 12 it gives 68.81%, 60.01% and 40.32% TOC removal for O3/UV/Persulfate, O3/UV and O3 process respectively. The result also reveals that decolorization of 98.95%, 95.17% and 94.71% was achieved by O3/UV/Persulfate, O3/UV and O3 process respectively. In addition to above, ozone consumption was also considerably decreased by 17% in case of O3/UV/Persulfate, as efficiency of process is enhanced by means of activation of persulfate through UV irradiation. Thus study reveals that mineralization follows: O3/UV/Persulfate> O3/UV> O3.

Keywords: AOP, mineralization, TOC, recalcitrant organic compounds

Procedia PDF Downloads 193

Authors: Sunil Kumar, Sandip Dhole, Deepak Salunke, Chung-ming Sun

Abstract:

Heterocycles bearing nitrogen, oxygen, and selenium are present in innumerable biologically active compounds. For instance, coumarin containing dicoumarol acts as naturally occurring anticoagulant. 2-Acylamido selenazole works as Store-Operated Calcium (SOC) channel regulator. Therefore, due to biologically significance of selenazole and coumarin and our quest to develop efficient methodologies for the synthesis of complex heterocycles, the trisubstituted angular isocoumarinoselenazole synthesis was proposed and achieved by starting from nitrobenzoic acid derivative, available commercially. Synthetic procedure involves three steps: i) the construction of 2-aminobenzoselenazoles, ii) their regioselective N-alkylation at position-2 and iii) alkyne insertion via Ru catalyzed C-H activation. Transition metal free synthesis of benzoselenazoles was successfully brought about by the addition/elimination reaction via intramolecular C-Se bond formation. In the next step, N-alkylation of selenazole furnished two regioisomers. Both the isomers exhibited different reactivity towards [4+2] alkyne annulation reaction. The fusion of α-pyrone ring on the benzo[1,3-d]selenazole skeleton was achieved via Ru(II)-catalyzed C-H activation and alkyne insertion. As evident from mechanism, the selenazole 'N' plays an important role for the experiential selectivity.

Keywords: alkylation, alkyne insertion, coumarin, selenazole

Procedia PDF Downloads 93

Authors: S. Melvin Samuel, Jayanta Bhattacharya

Abstract:

In the present study, a graphene oxide/chitosan (GO-CS) composite material was prepared and used as an adsorbent for the removal of methylene blue (MB) from aqueous solution. The synthesized GO-CS adsorbent was characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopes (SEM), transmission electron microscopy (TEM), Raman spectroscopy and thermogravimetric analysis (TGA). The removal of MB was conducted in batch mode. The effect of parameters influencing the adsorption of MB such as pH of the solution, initial MB concentration, shaking speed, contact time and adsorbent dosage were studied. The results showed that the GO-CS composite material has high adsorption capacity of 196 mg/g of MB solution at pH 9.0. Further, the adsorption of MB on GO-CS followed pseudo second order kinetics and equilibrium adsorption data well fitted by the Langmuir isotherm model. The study suggests that the GO-CS is a favorable adsorbent for the removal of MB from aqueous solution.

Keywords: Methylene blue, Graphene oxide-chitosan, Isotherms, Kinetics.

Procedia PDF Downloads 142

Authors: Sandip Sadhukhan, Arpita Sarkar, Debprasad Sinha, Goutam Kumar Ghorai, Gautam Sarkar, Ashis K. Dhara

Abstract:

Accurate segmentation of the optic disc is very important for computer-aided diagnosis of several ocular diseases such as glaucoma, diabetic retinopathy, and hypertensive retinopathy. The paper presents an accurate and fast optic disc detection and segmentation method using an attention based fully convolutional network. The network is trained from scratch using the fundus images of extended MESSIDOR database and the trained model is used for segmentation of optic disc. The false positives are removed based on morphological operation and shape features. The result is evaluated using three-fold cross-validation on six public fundus image databases such as DIARETDB0, DIARETDB1, DRIVE, AV-INSPIRE, CHASE DB1 and MESSIDOR. The attention based fully convolutional network is robust and effective for detection and segmentation of optic disc in the images affected by diabetic retinopathy and it outperforms existing techniques.

Keywords: attention-based fully convolutional network, optic disc detection and segmentation, retinal fundus image, screening of ocular diseases

Procedia PDF Downloads 102

Authors: Subodh N. Patel, Abhijit Pusty, Manashi Adhikary, Sandip Bhattacharyya

Abstract:

The steam superheater (SH) is a coil type heat exchanger which is used to produce superheated steam or to convert the wet steam to dry steam (69.6 kg/cm² and 495°C), generated by a boiler. There were two superheaters in the system, SH I and SH II. SH II is a set of tubes that faces the initial interaction with flue gas at high temperature followed by SH I tubes. After a service life of 2100 hours, a tube in the SH II found to be punctured. Dye penetrant test revealed that out of 50 such tubes, 14 more tubes had severe cracks at a similar location. The failure was investigated in detail. The materials and scale were characterized by optical microscope and advance characterization technique. Scale, observed on fracture surface, was characterized under scanning electron microscope and Raman spectroscopy. Stresses acting on the tubes in working condition were analyzed by finite element method software, ANSYS. Cyclic stresses were observed in the simulation at the same prone location due to restriction in expansion of tubes. Based on scale characterization and stress analysis, it was concluded that the tube failed in thermo-mechanical fatigue. Finally, prevention and control measures were taken to avoid such failure in the future.

Keywords: finite element analysis, oxide scale, superheater tube, thermomechanical fatigue

Procedia PDF Downloads 89

Authors: Sandip Tambare, Revati Ghadge

Abstract:

Alcohol withdrawal syndrome continue to be concerning health issue worldwide in alcoholics. Many current option for treating alcohol withdrawal signs are habit forming causing dependency of sedatives. The divine science of Ayurveda recommends Nasya for improvement of alcohol withdrawal signs. As per the latest reports 1/3 of the Indian population is using alcohol in an unhealthy manner, the complication being wide and varied among which, the Alcohol Withdrawal Syndrome is the dominant one. The presentation varies from mild sleep loss or anxiety to delirium. Ayurveda has given utmost in the context of Madatyaya(Alcoholism). Various protocols based on the identification of the status of tridoshas are explained which includes sodhana, samana and satwavachaya chikitsa. Various medications are being used, with appreciated effects in the clinical practice. As per reports, the panchakarma procedure nasya seems highly effective, in managing of the alcohol withdrawal syndrome. Nasya with Ksheerabala Taila is given for 7 days in the condition of Alcohol Withdrawal syndrome and it was the non Randomized trial with 30 subjects satisfying the DSM V criteria for alcohol withdrawl and the assessment was done using the Clinical Institute Withdrawal Assessment for Alcohol Scale revised (CIWA-Ar). Conclusion: Among the symptoms which were studied after the interventions, it was found that there was high significant response in almost all the symptoms in the given subjects. The eternal science of Ayurveda is able to answer the existing problem of alcohol and its abuse in the society.

Keywords: nasya, alcohol withdrawal, madatyaya, ksheerabala taila

Procedia PDF Downloads 96

Authors: Sandip Suman

Abstract:

Mechanical defects (cracks, voids, irregularities) in rocket motor propellant are not new and it is induced due to various reasons, which could be an improper manufacturing process, lot-to-lot variation in chemicals or just the natural aging of the products. These defects are normally identified during the examination of radiographic films by quality inspectors. However, a lot of times, these defects are under or over-classified by human inspectors, which leads to unpredictable performance during lot acceptance tests and significant economic loss. The human eye can only visualize larger cracks and defects in the radiographs, and it is almost impossible to visualize every small defect through the human eye. A different artificial intelligence-based machine vision methodology has been proposed in this work to identify and classify the structural defects in the radiographic films of rocket motors with solid propellant. The proposed methodology can extract the features of defects, characterize them, and make intelligent decisions for acceptance or rejection as per the customer requirements. This will automatize the defect detection process during manufacturing with human-like intelligence. It will also significantly reduce production downtime and help to restore processes in the least possible time. The proposed methodology is highly scalable and can easily be transferred to various products and processes.

Keywords: artificial intelligence, machine vision, defect detection, rocket motor propellant grains

Procedia PDF Downloads 61

Authors: Aniruddha Hore, Saptarshi Mitra, Sandip Ghosh, Sujoy Bose, Avijit Ghosh

Abstract:

The Indian rupee is the official currency of India. With time, science and technology got advanced, and our society is slowly making its way to a cashless mode of transaction. But as India is still a developing country, a large part of our society still depends on transaction through cash. During times of pandemics, we came to understand that everything that we touch is not safe from microbial contamination. The Indian currency is also not an exception. The Indian currency is the modern-day medium of harmful bacterial as well as other microbial contaminations resulting in diseases in human bodies. Therefore, the need came to make the currency disinfectant to give our people a healthier lifestyle. The main focus of the study is to develop a solution that, when applied to the currency notes, will kill the persisting bacteria or microbes present in the notes. So various natural edible products were used in order to prepare the solution, which is highly effective against the presence of harmful bacteria such as E. coli and S. aureus. The antibacterial activity of these natural ingredients is not unknown to us, so extracts from those products were mixed together to form a solution which was made the Indian currency notes antibacterial for 20min approx. The solution was creating a layer on the surface of currency notes, therefore, making it antibacterial for a given duration of time, i.e., no bacterial growth was seen during the time period of 20 minutes, therefore, making it safe for the usage of human hands.

Keywords: Indian currency, antibacterial property of Indian currency, surface coating, currency disinfectant

Procedia PDF Downloads 89

Authors: Yasaswi Vengalasetti, Jacob Eisenach, Jay Bhattacharya

Abstract:

Seroprevalence studies can provide an estimation of the Infection Fatality Rate (IFR), the probability of death given infection. Measuring the seroprevalence and reported deaths of an area within a given time frame an IFR can be estimated. With this IFR calculation, we can then observe COVID-19 death figures in different countries around the world and estimate the number of cases since the onset of the pandemic. There is a large range for estimated COVID-19 infections across different countries. This ranged from 0.659 million infections in Hong Kong to 277 million infections in India. The largest estimated share of the population infected is 63% in Peru and the lowest is 3% in Norway. For younger populations, COVID-19 is most fatal in South America; for older populations, it is most fatal in North America. The Asian regions stand out with significantly lower IFRs in older populations: at 80 years old, COVID-19 is about three times as fatal than in South Asia and about twelve times as fatal than in East Asia. The weighted average for the share of the population infected, the sum of infections divided by the sum of populations across all countries, is 23%.

Keywords: epidemiology, seroprevalence, covid-19, infection fatality rate

Procedia PDF Downloads 92

Authors: Abhishek Dixit, Sandip S. Sathe, Chandan Mahanta

Abstract:

The Siang river originates in Angsi glacier in southern Tibet (there known as the Yarlung Tsangpo). After traveling through Indus-Tsangpo suture zone and deep gorges near Namcha Barwa peak, it takes a south-ward turn and enters India, where it is known as Siang river and becomes a major tributary of the Brahmaputra in Assam plains. In this study, we have analyzed the bed sediment of the Siang river at two locations (one at extreme upstream near the India-China border and one downstream before Siang Brahmaputra confluence). We have also sampled bed sediment at the remote location of Yammeng river, an eastern tributary of Siang. The magnetic hysteresis properties show the combination of paramagnetic and weak ferromagnetic behavior with a multidomain state. Moreover, curie temperature analysis shows titanomagnetite solid solution series, which is causing the weak ferromagnetic signature. Given that the magnetic mineral was in a multidomain state, the presence of Ti, Fe carrying heave mineral, may be inferred. The Chemical index of alteration shows less weathered sediment. However, the Yammeng river sample being close to source shows fresh grains subjected to physical weathering and least chemically alteration. Enriched Ca and K and depleted Na and Mg with respect to upper continental crust concentration also points toward the less intense chemical weathering along with the dominance of calcite weathering.

Keywords: bed sediment, magnetic properties, Siang, weathering

Procedia PDF Downloads 91

Authors: Sandip Shrestha, Ann M. Donoghue, Komala Arsi, Basanta R. Wagle, Abhinav Upadhyay, Dan J. Donoghue

Abstract:

Campylobacter, one of the major cause of foodborne illness worldwide, is commonly present in the intestinal tract of poultry. Many strategies are currently being investigated to reduce Campylobacter counts on commercial poultry during processing with limited success. This study investigated the efficacy of the generally recognized as safe compound, carvacrol (CR), a component of wild oregano oil as a wash treatment for reducing C. jejuni and aerobic bacteria on chicken skin. A total of two trials were conducted, and in each trial, a total of 75 skin samples (4cm × 4cm each) were randomly allocated into 5 treatment groups (0%, 0.25%, 0.5%, 1% and 2% CR). Skin samples were inoculated with a cocktail of four wild strains of C. jejuni (~ 8 log10 CFU/skin). After 30 min of attachment, inoculated skin samples were dipped in the respective treatment solution for 1 min, allowed to drip dry for 2 min and processed at 0, 8, 24 h post treatment for enumeration of C. jejuni and aerobic bacterial counts (n=5/treatment/time point). The data were analyzed by ANOVA using PROC GLM procedure of SAS 9.3. All the tested doses of CR suspension consistently reduced C. jejuni counts across all time points. The 2% CR wash was the most effective treatment and reduced C. jejuni counts by ~4 log₁₀ CFU/sample (P < 0.05). Aerobic counts were reduced for the 0.5% CR dose at 0 and 24h in Trial 1 and at 0, 8 and 24h in Trial 2. The 1 and 2% CR doses consistently reduced aerobic counts in both trials up to 2 log₁₀ CFU/skin.

Keywords: Campylobacter jejuni, carvcrol, chicken skin, postharvest

Procedia PDF Downloads 144

Authors: Md. Sakinul Islam, Nhol Kao, Sati Bhattacharya, Rahul Gupta

Abstract:

The objective of the study is to produce naocrystalline cellulose (NCC) from rice husk by chemical extraction process. The chemical extraction processes of this production are delignification, bleaching and hydrolysis. In order to produce NCC, raw rice husk (RRH) was grinded and converted to powder form. Powder rice husk was obtained by sieving and the particles in the 75-710 μm size range was used for experimental work. The production of NCC was conducted into the jacketed glass reactor at 80 ˚C temperature under predetermined experimental conditions. In this work NaOH (4M) solution was used for delignification process. After certain experimental time delignified powder RH was collected from the reactor then washed, bleached and finally hydrolyzed in order to degrade cellulose to nanocrystalline cellulose (NCC). For bleaching and hydrolysis processes NaOCl (20%) and H2SO4 (4M) solutions were used, respectively. The resultant products from hydrolysis was neutralized by buffer solution and analyzed by FTIR, XRD, SEM, AFM and TEM. From the analysis, NCC has been identified successfully and the particle dimension has been confirmed to be in the range of 20-50 nm. From XRD results, the crystallinity of NCC was found to be approximately 45%.

Keywords: nanocrystalline cellulose, NCC, rice husk, biomass, chemical extraction

Procedia PDF Downloads 367

Authors: Ankur Gupta, Jayant Raj Saurav, Shantanu Bhattacharya

Abstract:

In this work we report an effective water filtration system based on the photo catalytic performance of semiconducting dense nano-brushes under natural sunlight. During thin-film photocatalysis usually performed by a deposited layer of photocatalyst, a stagnant boundary layer is created near the catalyst which adversely affects the rate of adsorption because of diffusional restrictions. One strategy that may be used is to disrupt this laminar boundary layer by creating a super dense nanostructure near the surface of the catalyst. Further it is adequate to fabricate a structured filter element for a through pass of the water with as grown nanostructures coming out of the surface of such an element. So, the dye remediation is performed through solar means. This remediation was initially limited to lower efficiency because of diffusional restrictions but has now turned around as a fast process owing to the development of the filter materials with standing out dense nanostructures. The effect of increased surface area due to microholes on fraction adsorbed is also investigated and found that there is an optimum value of hole diameter for maximum adsorption.

Keywords: nano materials, photocatalysis, waste water treatment, water remediation

Procedia PDF Downloads 301

Authors: Jonardan Koner, Basabi Bhattacharya, Avinash Purandare

Abstract:

The study is focused to find out the impact of infrastructural investment on economic development in Indian states. The study uses panel data analysis to measure the impact of infrastructural investment on Real Gross Domestic Product in Indian States. Panel data analysis incorporates Unit Root Test, Cointegration Teat, Pooled Ordinary Least Squares, Fixed Effect Approach, Random Effect Approach, Hausman Test. The study analyzes panel data (annual in frequency) ranging from 1991 to 2012 and concludes that infrastructural investment has a desirable impact on economic development in Indian. Finally, the study reveals that the infrastructural investment significantly explains the variation of economic indicator.

Keywords: infrastructural investment, real GDP, unit root test, cointegration teat, pooled ordinary least squares, fixed effect approach, random effect approach, Hausman test

Procedia PDF Downloads 372

Authors: Tharntip Tawnie Chutikulrungsee, Oliver Kisalay Burmeister, Maumita Bhattacharya, Dragana Calic

Abstract:

Sharing on social network sites (SNSs) has rapidly emerged as a new social norm and has become a global phenomenon. Billions of users reveal not only their own information (self disclosure) but also information about others (other-generated disclosure), resulting in a risk and a serious threat to either personal or informational privacy. Self-disclosure (SD) has been extensively researched in the literature, particularly regarding control of individual and existing privacy management. However, far too little attention has been paid to other-generated disclosure (OGD), especially by insiders. OGD has a strong influence on self-presentation, self-image, and electronic word of mouth (eWOM). Moreover, OGD is more credible and less likely manipulated than SD, but lacks privacy control and legal protection to some extent. This article examines OGD in depth, ranging from motivation to both online and offline impacts, based upon lived experiences from both ‘the disclosed’ and ‘the discloser’. Using purposive sampling, this phenomenological study involves an online survey and in-depth interviews. The findings report the influence of peer disclosure as well as users’ strategies to mitigate privacy issues. This article also calls attention to the challenge of OGD privacy and inadequacies in the law related to privacy protection in the digital domain.

Keywords: facebook, online privacy, other-generated disclosure, social networks sites (SNSs)

Procedia PDF Downloads 220

Authors: A. Bhattacharya, Sanjay Gupta, S. H. Bodakhe

Abstract:

HbA1c is form of the haemoglobin that is used to measure the average plasma glucose concentration over prolonged periods of time. It is formed in a non-enzymatic glycation pathway by hemoglobin's exposure to plasma glucose. In diabetes mellitus, higher amounts of glycated hemoglobin, indicating poorer control of blood glucose levels, have been associated with cardiovascular disease, nephropathy, and retinopathy. Guraku’s basic components are nicotine and jaggery, jaggery is made up of sugarcane so can have a diabetogenic potential which is exacerbated in presence of nicotine. This work had done with the aim to find correlation between Diabetic cataract, HbA1c and Guraku. Subjects were enrolled according to the inclusion and exclusion criteria. In this study total 75 subjects were included. In the study it was found that people consuming Guraku had a high level of HbA1c thus are more prone to the development of diabetic cataract. Male subjects are the more than female subjects. Most of the subjects belong to the lower socioeconomical class and not very educated. It could be concluded that this type of study could be useful in indentifying number of subjects suffering from diabetic cataract whose condition get worse by use of nicotine product like Guraku and preventive measure to be taken in prevention of this type of diabetic complication.

Keywords: diabetic cataract, HbA1c, Guraku, diabetogenic potential

Procedia PDF Downloads 373

Authors: Manendra Singh Parihar, Sandip Ghosh Chowdhury

Abstract:

Austenitic stainless steels are widely used and give a good combination of properties. When this steel is plastically deformed, a phase transformation of the metastable Face Centred Cubic Austenite to the stable Body Centred Cubic (α’) or to the Hexagonal close packed (ԑ) martensite may occur, leading to the enhancement in the mechanical properties like strength. The work was based on variant selection and corresponding texture analysis for the strain induced martensitic transformation during deformation of the parent austenite FCC phase to form the product HCP and the BCC martensite phases separately, obeying their respective orientation relationships. The automated method for reconstruction of the parent phase orientation using the EBSD data of the product phase orientation is done using the MATLAB and TSL-OIM software. The method of triplets was used which involves the formation of a triplet of neighboring product grains having a common variant and linking them using a misorientation-based criterion. This led to the proper reconstruction of the pre-transformation phase orientation data and thus to its microstructure and texture. The computational speed of current method is better compared to the previously used methods of reconstruction. The reconstruction of austenite from ԑ and α’ martensite was carried out for multiple samples and their IPF images, pole figures, inverse pole figures and ODFs were compared. Similar type of results was observed for all samples. The comparison gives the idea for estimating the correct sequence of the transformation i.e. γ → ε → α’ or γ → α’, during deformation of AISI 304 austenitic stainless steel.

Keywords: variant selection, reconstruction, EBSD, austenitic stainless steel, martensitic transformation

Procedia PDF Downloads 459

Authors: Manendra Singh Parihar, Sandip Ghosh Chowdhury

Abstract:

Austenitic stainless steels are widely used and give a good combination of properties. When this steel is plastically deformed, a phase transformation of the metastable Face Centred Cubic Austenite to the stable Body Centred Cubic (α’) or to the Hexagonal close packed (ԑ) martensite may occur, leading to the enhancement in the mechanical properties like strength. The work was based on variant selection and corresponding texture analysis for the strain induced martensitic transformation during deformation of the parent austenite FCC phase to form the product HCP and the BCC martensite phases separately, obeying their respective orientation relationships. The automated method for reconstruction of the parent phase orientation using the EBSD data of the product phase orientation is done using the MATLAB and TSL-OIM software. The method of triplets was used which involves the formation of a triplet of neighboring product grains having a common variant and linking them using a misorientation-based criterion. This led to the proper reconstruction of the pre-transformation phase orientation data and thus to its micro structure and texture. The computational speed of current method is better compared to the previously used methods of reconstruction. The reconstruction of austenite from ԑ and α’ martensite was carried out for multiple samples and their IPF images, pole figures, inverse pole figures and ODFs were compared. Similar type of results was observed for all samples. The comparison gives the idea for estimating the correct sequence of the transformation i.e. γ → ε → α’ or γ → α’, during deformation of AISI 304 austenitic stainless steel.

Keywords: variant selection, reconstruction, EBSD, austenitic stainless steel, martensitic transformation

Procedia PDF Downloads 461