Search results for: Piyachat Chuysinuan

Authors: Piyachat Chuysinuan, Nitirat Chimnoi, Arthit Makarasen, Nanthawan Reuk-Ngam, Pitt Supaphol, Supanna Techasakul

Abstract:

In this work, biomaterial wound dressings was developed based on gelatin containing herbal substances (essential oil), a substance from the plant Eupatorium adenophorum Spreng (Crofton weed) that used as traditional wound healers. Gelatin hydrogel was prepared from a 10 wt-% gelatin solution. The oil in water (o/w) emulsion Eupatorium adenophorum of essential oil were prepared and used Pluronic F68 as a surfactant. The 10, 20, and 30 % v/v emulsion were mixed with gelatin solution and cast into film. These hydrogels were tested for their gel fraction, swelling and weight loss behavior. With an increase in the emulsion concentration the emulsion-loaded in hydrogels, the gel fraction were decreased due to the crosslink density, while the swelling and weight loss behavior were increased with an increasing in the emulsion content. The potential to use the emulsion-containing gelatin hydrogels as wound dressing was assessed on investigation the release characteristics of the as-loaded hydrogels. The E. adenophorum essential oil was first identified the chemical composition by using GC-MS analysis. The principal components of the oil were p-cymene (16.23%), bornyl acetate (11.84%), and amorpha-4, 7(11)-diene (10.51%). The hydrogel wound dressing containing essential oil was then characterized for their antibacterial activity against Gram-positive and Gram-negative in order to elucidate their potential for use as antibacterial wound dressings by using agar disk diffusion methods. The result showed that E. adenophorum essential oil and the emulsion-loaded gelatin hydrogel inhibited the growth of the test pathogens, Staphylococcus aureus and Staphylococcus epidermidis and increased with increasing the initial amount of essential oil in the hydrogels which confirmed their application as antibacterial wound dressings. Furthermore, the potential use of these wound dressings was further assessed in terms of the indirect cytotoxicity, in vitro attachment and proliferation of dermal human fibroblasts cultured in the hydrogel wound dressings.

Keywords: hydrogel, antibacterial wound dressing, Eupatorium adenophorum essential oil, gelatin

Procedia PDF Downloads 310

Authors: Patcharakamon Nooeaid, Piyachat Chuysrinuan

Abstract:

Electrospun natural polymers-based nanofibers are one of the most interesting materials used in tissue engineering and drug delivery applications. Bead-on-string nanofibers have gained considerable interest for sustained drug release. Vancomycin was used as the model drug and sodium alginate (SA)/soy protein isolated (SPI) as the polymer blend to fabricate the bead-on-string nanofibers by aqueous-based electrospinning. The bead-on-string SA/SPI nanofibers were successfully fabricated by the addition of poly(ethylene oxide) (PEO) as a co-blending polymer. SA-PEO with mass ratio of 70/30 showed the best spinnability with continuous nanofibers without the occurrence of beads. Bead structure formed with the addition of SPI and bead number increased with increasing SPI content. The electrospinning of 80/20 SA-PEO/SPI was obtained as a great promising bead-on-string nanofibers for drug loading, while the solution of 50/50 was not able to obtain continuous fibers. In vitro release tests showed that a more sustainable release profile up to 14 days with less initial burst release on day 1 could be obtained from the bead-on-string fibers than from smooth fibers with uniform diameter. In addition, vancomycin-loaded beaded fibers inhibited the growth of Staphylococcus aureus (S. aureus) bacteria. Therefore, the SA-PEO/SPI nanofibers showed the potential to be used as biomaterials for tissue engineering and drug delivery.

Keywords: bead-on-string fibers, electrospinning, drug delivery, tissue engineering

Procedia PDF Downloads 301