Search results for: Konstanty Skalski

Authors: Marek Pawlikowski, Krzysztof Jankowski, Konstanty Skalski, Anna Makuch

Abstract:

Nanoindentation or depth-sensing indentation (DSI) technique has proven to be very useful to measure mechanical properties of various tissues at a micro-scale. Bone tissue, both trabecular and cortical one, is one of the most commonly tested tissues by means of DSI. Most often such tests on bone samples are carried out to compare the mechanical properties of lamellar and interlamellar bone, osteonal bone as well as compact and cancellous bone. In the paper, a relation between stress and strain for human trabecular bone is presented. The relation is based on the results of nanoindentation tests. The formulation of a constitutive model for human trabecular bone is based on nanoindentation tests. In the study, the approach proposed by Olivier-Pharr is adapted. The tests were carried out on samples of trabecular tissue extracted from human femoral heads. The heads were harvested during surgeries of artificial hip joint implantation. Before samples preparation, the heads were kept in 95% alcohol in temperature 4 Celsius degrees. The cubic samples cut out of the heads were stored in the same conditions. The dimensions of the specimens were 25 mm x 25 mm x 20 mm. The number of 20 samples have been tested. The age range of donors was between 56 and 83 years old. The tests were conducted with the indenter spherical tip of the diameter 0.200 mm. The maximum load was P = 500 mN and the loading rate 500 mN/min. The data obtained from the DSI tests allows one only to determine bone behoviour in terms of nanoindentation force vs. nanoindentation depth. However, it is more interesting and useful to know the characteristics of trabecular bone in the stress-strain domain. This allows one to simulate trabecular bone behaviour in a more realistic way. The stress-strain curves obtained in the study show relation between the age and the mechanical behaviour of trabecular bone. It was also observed that the bone matrix of trabecular tissue indicates an ability of energy absorption.

Keywords: constitutive model, mechanical behaviour, nanoindentation, trabecular bone

Procedia PDF Downloads 222

Authors: Anna Makuch, Grzegorz Kokot, Konstanty Skalski, Jakub Banczorowski

Abstract:

Cancellous bone is a porous composite of a hierarchical structure and anisotropic properties. The biological tissue is considered to be a viscoelastic material, but many studies based on a nanoindentation method have focused on their elasticity and microhardness. However, the response of many organic materials depends not only on the load magnitude, but also on its duration and time course. Depth Sensing Indentation (DSI) technique has been used for examination of creep in polymers, metals and composites. In the indentation tests on biological samples, the mechanical properties are most frequently determined for animal tissues (of an ox, a monkey, a pig, a rat, a mouse, a bovine). However, there are rare reports of studies of the bone viscoelastic properties on microstructural level. Various rheological models were used to describe the viscoelastic behaviours of bone, identified in the indentation process (e. g Burgers model, linear model, two-dashpot Kelvin model, Maxwell-Voigt model). The goal of the study was to determine the influence of creep effect on the mechanical properties of human cancellous bone in indentation tests. The aim of this research was also the assessment of the material properties of bone structures, having in mind the energy aspects of the curve (penetrator loading-depth) obtained in the loading/unloading cycle. There was considered how the different holding times affected the results within trabecular bone.As a result, indentation creep (CIT), hardness (HM, HIT, HV) and elasticity are obtained. Human trabecular bone samples (n=21; mean age 63±15yrs) from the femoral heads replaced during hip alloplasty were removed and drained from alcohol of 1h before the experiment. The indentation process was conducted using CSM Microhardness Tester equipped with Vickers indenter. Each sample was indented 35 times (7 times for 5 different hold times: t1=0.1s, t2=1s, t3=10s, t4=100s and t5=1000s). The indenter was advanced at a rate of 10mN/s to 500mN. There was used Oliver-Pharr method in calculation process. The increase of hold time is associated with the decrease of hardness parameters (HIT(t1)=418±34 MPa, HIT(t2)=390±50 MPa, HIT(t3)= 313±54 MPa, HIT(t4)=305±54 MPa, HIT(t5)=276±90 MPa) and elasticity (EIT(t1)=7.7±1.2 GPa, EIT(t2)=8.0±1.5 GPa, EIT(t3)=7.0±0.9 GPa, EIT(t4)=7.2±0.9 GPa, EIT(t5)=6.2±1.8 GPa) as well as with the increase of the elastic (Welastic(t1)=4.11∙10-7±4.2∙10-8Nm, Welastic(t2)= 4.12∙10-7±6.4∙10-8 Nm, Welastic(t3)=4.71∙10-7±6.0∙10-9 Nm, Welastic(t4)= 4.33∙10-7±5.5∙10-9Nm, Welastic(t5)=5.11∙10-7±7.4∙10-8Nm) and inelastic (Winelastic(t1)=1.05∙10-6±1.2∙10-7 Nm, Winelastic(t2) =1.07∙10-6±7.6∙10-8 Nm, Winelastic(t3)=1.26∙10-6±1.9∙10-7Nm, Winelastic(t4)=1.56∙10-6± 1.9∙10-7 Nm, Winelastic(t5)=1.67∙10-6±2.6∙10-7)) reaction of materials. The indentation creep increased logarithmically (R2=0.901) with increasing hold time: CIT(t1) = 0.08±0.01%, CIT(t2) = 0.7±0.1%, CIT(t3) = 3.7±0.3%, CIT(t4) = 12.2±1.5%, CIT(t5) = 13.5±3.8%. The pronounced impact of creep effect on the mechanical properties of human cancellous bone was observed in experimental studies. While the description elastic-inelastic, and thus the Oliver-Pharr method for data analysis, may apply in few limited cases, most biological tissues do not exhibit elastic-inelastic indentation responses. Viscoelastic properties of tissues may play a significant role in remodelling. The aspect is still under an analysis and numerical simulations. Acknowledgements: The presented results are part of the research project founded by National Science Centre (NCN), Poland, no.2014/15/B/ST7/03244.

Keywords: bone, creep, indentation, mechanical properties

Procedia PDF Downloads 172

Authors: K. Jankowski, M. Pawlikowski, A. Makuch, K. Skalski

Abstract:

Depth-sensing indentation (DSI) or nanoindentation is becoming a more and more popular method of measuring mechanical properties of various materials and tissues at a micro-scale. This technique allows measurements without complicated sample preparation procedures which makes this method very useful. As a result of measurement force and displacement of the intender are obtained. It is also possible to determine three measures of hardness i.e. Martens hardness (HM), nanohardness (HIT), Vickers hardness (HV) and Young modulus EIT. In this work trabecular bone mechanical properties were investigated. The bone samples were harvested from human femoral heads during hip replacement surgery. Patients were of different age, sexes and stages of tissue degeneration caused by osteoarthritis. The specimens were divided into three groups. Each group contained samples harvested from patients of different range of age. All samples were investigated with the same measurement conditions. The maximum load was Pmax=500 mN and the loading rate was 500 mN/min. The tests were held without hold at the peak force. The tests were conducted with indenter Vickers tip and spherical tip of the diameter 0.2 mm. Each trabecular bone sample was tested 7 times in a close area of the same trabecula. The measured loading P as a function of indentation depth allowed to obtain hysteresis loop and HM, HIT, HV, EIT. Results for arbitrarily chosen sample are HM=289.95 ± 42.31 MPa, HIT=430.75 ± 45.37 MPa, HV=40.66 ± 4.28 Vickers, EIT=7.37 ± 1.84 GPa for Vickers tip and HM=115.19 ± 15.03 MPa, HIT=165.80 ± 19.30 MPa, HV=16.90 ± 1.97 Vickers, EIT=5.30 ± 1.31 GPa for spherical tip. Results of nanoindentation tests show that this method is very useful and is perfect for obtaining mechanical properties of trabecular bone. Estimated values of elastic modulus are similar. The differences between hardness are significant but it is a result of using two different types of tips. However, it has to be emphasised that the differences in the values of elastic modulus and hardness result from different testing protocols, anisotropy and asymmetry of the micro-samples and the hydration of bone.

Keywords: human bone, mechanical properties, nano hardness nanoindentation, trabecular bone

Procedia PDF Downloads 276