Osteoporosis is a multifactorial disease that results in reduced quality of life, causes decreased bone strength, and changes in their microarchitecture. Mostly postmenopausal women are at risk. In our study, we measured anthropometric parameters of postmenopausal women (104 women of control group – CG and 105 women of osteoporotic group - OG) and determined TSH hormone levels and PTH as well as mineral elements - Ca, P, Mg and enzyme alkaline phosphatase. Through the correlation analysis in CG, we have found association based on age and BMI, P and Ca, as well as Mg and Ca; in OG we determined interdependence based on an association of age and BMI, age and Ca. Using the Student's t test, we found significantly important differences in biochemical parameters of Mg (p ˂ 0,001) and TSH (p ˂ 0,05) between CG and OG.

Keywords: factors, bone mass density, Central Europe, biomarkers

Procedia PDF Downloads 162

1 The Effect of Calcining Temperature on Photocatalytic Activity of Porous ZnO Architecture

Authors: M. Masar, P. Janota, J. Sedlak, M. Machovsky, I. Kuritka

Abstract:

Zinc oxide (ZnO) nano crystals assembled porous architecture was prepared by thermal decomposition of zinc oxalate precursor at various temperatures ranging from 400-900°C. The effect of calcining temperature on structure and morphology was examined by scanning electron microscopy (SEM), X-ray diffractometry, thermogravimetry, and BET adsorption analysis. The porous nano crystalline ZnO morphology was developed due to the release of volatile precursor products, while the overall shape of ZnO micro crystals was retained as a legacy of the precursor. The average crystallite size increased with increasing temperature of calcination from approximately 21 nm to 79 nm, while the specific surface area decreased from 30 to 1.7 m2g-1. The photo catalytic performance of prepared ZnO powders was evaluated by degradation of methyl violet 2B, a model compound. The significantly highest photo catalytic activity was achieved with powder calcined at 500°C. This may be attributed to the sufficiently well-developed crystalline arrangement, while the specific surface area is still high enough.

Keywords: ZnO, porous structure, photodegradation, methyl violet

Procedia PDF Downloads 373