Authors: Alparslan A. Balta, Hilmi Yurdakul, Orkun Tunckan, Servet Turan, Arife Yurdakul

Abstract:

Si2N2O (Sinoite) is an inorganic-based oxynitride material that reveals promising phosphor candidates for white light-emitting diodes (WLEDs). However, there is now limited knowledge to explain the synthesis of Si2N2O for this purpose. Here, to the best of authors’ knowledge, we report the first time the production of Si2N2O based phosphors by CeO2, SiO2, Si3N4 from main starting powders, and Li2O sintering additive through spark plasma sintering (SPS) route. The processing parameters, e.g., pressure, temperature, and sintering time, were optimized to reach the monophase Si2N2O containing samples. The lattice parameter, crystallite size, and amount of formation phases were characterized in detail by X-ray diffraction (XRD). Grain morphology, particle size, and distribution were analyzed by scanning and transmission electron microscopes (SEM and TEM). Cathodoluminescence (CL) in SEM and photoluminescence (PL) analyses were conducted on the samples to determine the excitation, and emission characteristics of Ce3+ activated Si2N2O. Results showed that the Si2N2O phase in a maximum 90% ratio was obtained by sintering for 15 minutes at 1650oC under 30 MPa pressure. Based on the SEM-CL and PL measurements, Ce3+: Si2N2O phosphor shows a broad emission summit between 400-700 nm that corresponds to white light. The present research was supported by TUBITAK under project number 217M667.

Keywords: cerium, oxynitride, phosphors, sinoite, Si₂N₂O

Procedia PDF Downloads 79

Authors: Alparslan A. Balta, Hilmi Yurdakul, Orkun Tunckan, Servet Turan, Arife Yurdakul

Abstract:

A silicon oxynitride (Si2N2O), the mineralogical name is “Sinoite”, reveals the outstanding physical, mechanical and thermal properties, e.g., good oxidation resistance at high temperatures, high fracture toughness with rod shape, high hardness, low theoretical density, good thermal shock resistance by low thermal expansion coefficient and high thermal conductivity. In addition, the orthorhombic crystal structure of Si2N2O allows accommodating the rare earth (RE) element atoms along the “c” axis due to existing large structural interstitial sites. Here, 0.02 to 0.12 wt. % Nd3+ doped Si2N2O samples were successfully synthesized by spark plasma sintering (SPS) method at 30MPa pressure and 1650oC temperature. Li2O was also utilized as a sintering additive to take advantage of low eutectic point during synthesizing. The specimens were characterized in detail by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and cathodoluminescence (CL) in SEM and photoluminescence (PL) spectroscopy. Based on the overall results, the Si2N2O phase was obtained above 90% by the SPS route. Furthermore, Nd3+: Si2N2O samples showed a very broad intense emission peak between 400-700 nm, which corresponds to white color. Therefore, this material can be considered as a promising candidate for white light-emitting diodes (WLEDs) purposes. This study was supported by TUBITAK under project number 217M667.

Keywords: neodymium, oxynitride, Si₂N₂O, WLEDs

Procedia PDF Downloads 102

Authors: Arife Simsek, Gulfem Bakan

Abstract:

Sediment refers to the accumulation of varying amounts of sediment material in natural waters and the formation of bottom sludge. Sediments are the most important sources of pollutants as well as important future sources and carriers of pollutants. The accumulation of pollutants in sediments can cause serious environmental problems for the surrounding areas. Heavy metals (such as Cr, Cd, Al, Pb, Cu, Al, Zn) disrupt the water quality, affect the useful use of sediment, affect the ecosystem and have a toxic effect on the life of the sediment layer. This effect, which accumulates in the aquatic organisms, can enter the human body with the food chain and affect health seriously. Potential metal toxicity can be determined by comparing acid volatile sulfides (AVS) – simultaneously extracted metal (SEM) ratio in anoxic sediments to determine the effect of metals. Determination of the concentration of SEM and AVS is useful in screening sediments for potential toxicity due to the high metal concentration. In the case of SEM/AVS < 0 (anoxic sediment); in terms of AVS biomass production, its toxicity can be controlled. No toxic effects may be observed when SEM / AVS < 0. SEM / AVS > 0 (in the case of oxic sediment); metals with sensitive fraction such as Cu, As, Ag, Zn are stored. In this study, AVS and SEM measurements of sediment samples collected from five different points in the district of Tekkeköy in Samsun province were performed. The SEM - AVS ratio was greater than 0 in all samples. Therefore, it is necessary to test the toxicity against the risks that may occur in the ecosystem.

Keywords: AVS-SEM, Black Sea, heavy metal, sediment, toxicity

Procedia PDF Downloads 103

Authors: Saylav Ejder Bora, Arife Erdogan, Mumin Alper Erdogan, Oytun Erbas, Ismet Parlak

Abstract:

Objective: The aim of this study was to evaluate histological, electrical and biochemical effects of metoprolol, lipid emulsion and magnesium sulphate as an alternative method to be used in preventing long QT emergence, that is among the lethal consequences of amitryptiline toxicity. Methods: Thirty Sprague- Dawley male rats were included. Rats were randomly separated into 5 groups. First group was administered saline only while the rest had received amitryptiline 100 mg/kg + saline, 5 mg/kg metoprolol, 20 ml/kg lipid emulsion and 75 mg/kg magnesium sulphate (MgSO4) intraperitoneally. ECG at DI lead, biochemical tests following euthanasia were performed in all groups after 1 hour of administration. Cardiac tissues were removed, sections were prepared and examined. Results: QTc values were significantly shorter in the rest when compared to amitryptiline+ saline group. While lipid emulsion did not affect proBNP and troponin values biochemically as compared to that of the control group, histologically, it was with reduced caspase 3 expression. Though statistically insignificant in the context of biochemical changes, pro-BNP and urea levels were lower in the metoprolol group when compared to controls. Similarly, metoprolol had no statistically significant effect on histological caspase 3 expression in the group that was treated with amitryptiline+metoprolol. On the other hand, there was a statistically significant decrease in Troponin, pro-BNP and urea levels as well as significant decline in histological caspase 3 expression within the MgSO4 group when compared to controls. Conclusion: As still a frequent cause of mortality in emergency units, administration of MgSO4, lipid emulsion and metoprolol might be beneficial in alternative treatment of cardiovascular toxicity caused by tricyclic antidepressant overdose, whether intake would be intentional or accidental.

Keywords: amitryptiline, cardiovascular toxicity, long QT, Rat Model

Procedia PDF Downloads 149