	%X This paper presents the results of an experimental
investigation carried out to evaluate the shrinkage of High Strength
Concrete. High Strength Concrete is made by partially replacement of
cement by flyash and silica fume. The shrinkage of High Strength
Concrete has been studied using the different types of coarse and fine
aggregates i.e. Sandstone and Granite of 12.5 mm size and Yamuna
and Badarpur Sand. The Mix proportion of concrete is 1:0.8:2.2 with
water cement ratio as 0.30. Superplasticizer dose @ of 2% by weight
of cement is added to achieve the required degree of workability in
terms of compaction factor.
From the test results of the above investigation it can be concluded
that the shrinkage strain of High Strength Concrete increases with
age. The shrinkage strain of concrete with replacement of cement by
10% of Flyash and Silica fume respectively at various ages are more
(6 to 10%) than the shrinkage strain of concrete without Flyash and
Silica fume. The shrinkage strain of concrete with Badarpur sand as
Fine aggregate at 90 days is slightly less (10%) than that of concrete
with Yamuna Sand. Further, the shrinkage strain of concrete with
Granite as Coarse aggregate at 90 days is slightly less (6 to 7%) than
that of concrete with Sand stone as aggregate of same size. The
shrinkage strain of High Strength Concrete is also compared with that
of normal strength concrete. Test results show that the shrinkage
strain of high strength concrete is less than that of normal strength
concrete.
	%P 154 - 157