Fracture Characterization of Plain Woven Fabric Glass-Epoxy Composites

Authors: Sabita Rani Sahoo, A.Mishra

Abstract:

Delamination between layers in composite materials is a major structural failure. The delamination resistance is quantified by the critical strain energy release rate (SERR). The present investigation deals with the strain energy release rate of two woven fabric composites. Materials used are made of two types of glass fiber (360 gsm and 600 gsm) of plain weave and epoxy as matrix. The fracture behavior is studied using the mode I, double cantilever beam test and the mode II, end notched flexure test, in order to determine the energy required for the initiation and growth of an artificial crack. The delamination energy of these two materials is compared in order to study the effect of weave and reinforcement on mechanical properties. The fracture mechanism is also analyzed by means of scanning electron microscopy (SEM). It is observed that the plain weave fabric composite with lesser strand width has higher inter laminar fracture properties compared to the plain weave fabric composite with more strand width.

Keywords: Glass- epoxy composites, Fracture Tests: mode I (DCB) and mode II (ENF), Delamination, Calculation of strain energy release rate, SEM Analysis

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1062796

References:

[1] Pandita, Surya D, Gert Huysmans, Martine Wevers, Ignaas Verpoest, "Tensile fatigue damage development in Plain weave and knitted Fabric Composites (gfrp)", Department of Metallurgy and Materials Engineering, Katholieke Universiteit Leuven, De Croylaan 2, B-3001 Leuven, Belgium, 2000.
[2] Blackman, B. R. K., and Kinloch, A. J., "Protocol for the Determination of the Mode I Adhesive Fracture Energy, GIC, of Structural Adhesives Using the Double Cantilever Beam (DCB) and Tapered Double Cantilever Beam (TDCB) Specimens," European structural integritysociety-polymers, adhesives and composites TC4 Committee (Version 00-0822- 06-00), 2001.
[3] Bolotin, V. V., "Mechanics of Delamination in Laminate Composite Structures", Mech. Compos Mater., 37, 2001,pp. 367-380.
[4] Naik, N. K., Reddy, K. S., "Interlaminar fracture characterization for plain weave fabric composites Mechanics of Composite Materials," Vol. 37, Nos. 5/6, 2001.
[5] S├©rensen Bent F., Kenneth J├©rgensen, Torben K. Jacobsen, and Rasmus C. ├ÿstergaard, "A general mixed mode fracture mechanics test specimen: The DCB-specimen loaded with uneven bending moments",Materials Research Department, Ris├© National Laboratory, 4000 Roskilde, Denmark LM Glasfiber Rolles M├©llevej 1, DK-6640 Lunderskov, Denmark, March 2004..
[6] Zenasni, R., Bachir, A. S., Arg├╝elles, A. M., Castrillo, Vi├▒a,A., J. 1, "Fracture Characterization of Woven Fabric Reinforced Thermoplastic Composites," Journal of Engineering Materials and Technology April 2007, Vol. 129 / 193.
[7] Zulkifli Rozli, Che Husna Azhari, Mohd Jailani Mohd Nor And Simin Oshkovr, "The effect of plies and processing time on mode I and mode III fracture properties of woven silk fibre/polyester composites," Department of Mechanical and Materials Engineering, 2008.
[8] Marat-Mendes, R.M.M., and M.M. de Freitas, "Characterization of Delamination Fracture Surfaces Under Mixed Mode Loading", Escola Superior de Tecnologia de Set├║bal, Campus do IPS, Estefanilha, 2910- 761, Set├║bal, Portugal , 2008.
[9] Singla Manoj-1 and Vikas Chawla-2, "Mechanical Properties of Epoxy Resin - Fly Ash Composite," 1-Department of Mechanical Engineering, R.I.E.I.T., Railmajra, Distt. Nawanshahr (Pb.)- 144533, INDIA, 2. Department of Materials & Metallurgical Engineering, I.I.T. Roorkee (Uttaranchal), INDIA, 2010, Vol. 9,No.3, pp.199-210.
[10] ASTM D 5528, Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fibre-Reinforced Polymer Matrix Composite,"Annual Book of ASTM Standards," ASTM, West Conshohoken, Pennsylvania, 14.02, 2001, pp. 272-281.