	%T A Study on Cement-Based Composite Containing Polypropylene Fibers and Finely Ground Glass Exposed to Elevated Temperatures
	%U https://publications.waset.org/pdf/1327
	%V 10
	%X High strength concrete has been used in situations
where it may be exposed to elevated temperatures. Numerous authors
have shown the significant contribution of polypropylene fiber to the
spalling resistance of high strength concrete.
When cement-based composite that reinforced by polypropylene
fibers heated up to 170 °C, polypropylene fibers readily melt and
volatilize, creating additional porosity and small channels in to the
matrix that cause the poor structure and low strength.
This investigation develops on the mechanical properties of mortar
incorporating polypropylene fibers exposed to high temperature.
Also effects of different pozzolans on strength behaviour of samples
at elevated temperature have been studied.
To reach this purpose, the specimens were produced by partial
replacement of cement with finely ground glass, silica fume and rice
husk ash as high reactive pozzolans. The amount of this replacement
was 10% by weight of cement to find the effects of pozzolans as a
partial replacement of cement on the mechanical properties of
mortars. In this way, lots of mixtures with 0%, 0.5%, 1% and 1.5% of
polypropylene fibers were cast and tested for compressive and
flexural strength, accordance to ASTM standard. After that
specimens being heated to temperatures of 300, 600 °C, respectively,
the mechanical properties of heated samples were tested.
Mechanical tests showed significant reduction in compressive
strength which could be due to polypropylene fiber melting. Also
pozzolans improve the mechanical properties of sampels.
	%P 94 - 99