%0 Journal Article %A Wipada Ploysuksai and Pramoch Rangsunvigit and Santi Kulprathipanja %D 2012 %J International Journal of Materials and Metallurgical Engineering %B World Academy of Science, Engineering and Technology %I Open Science Index 64, 2012 %T Effects of TiO2 and Nb2O5 on Hydrogen Desorption of Mg(BH4)2 %U https://publications.waset.org/pdf/12754 %V 64 %X In this work, effects of catalysts (TiO2, and Nb2O5) were investigated on the hydrogen desorption of Mg(BH4)2. LiBH4 and MgCl2 with 2:1 molar ratio were mixed by using ball milling to prepare Mg(BH4)2. The desorption behaviors were measured by thermo-volumetric apparatus. The hydrogen desorption capacity of the mixed sample milled for 2 h was 4.78 wt% with a 2-step released. The first step occurred at 214 °C and the second step appeared at 374 °C. The addition of 16 wt% Nb2O5 decreased the desorption temperature in the second step about 66 °C and increased the hydrogen desorption capacity to 4.86 wt% hydrogen. The addition of TiO2 also improved the desorption temperature in the second step and the hydrogen desorption capacity. It decreased the desorption temperature about 71°C and showed a high amount of hydrogen, 5.27 wt%, released from the mixed sample. The hydrogen absorption after desorption of Mg(BH4)2 was also studied under 9.5 MPa and 350 °C for 12 h. %P 311 - 315