	%T Effect of Adding Sawdust on Mechanical- Physical Properties of Ceramic Bricks to Obtain Lightweight Building Material
	%U https://publications.waset.org/pdf/11497
	%V 71
	%X This paper studies the application of a variety of
sawdust materials in the production of lightweight insulating bricks.
First, the mineralogical and chemical composition of clays was determined. Next, ceramic bricks were fabricated with different
quantities of materials (3–6 and 9 wt. % for sawdust, 65 wt. % for grey clay, 24–27 and 30 wt. % for yellow clay and 2 wt% of tuff).
These bricks were fired at 800 and 950 °C. The effect of adding this sawdust on the technological behaviour of the brick was assessed by
drying and firing shrinkage, water absorption, porosity, bulk density
and compressive strength. The results have shown that the optimum
sintering temperature is 950 °C. Below this temperature, at 950 °C,
increased open porosity was observed, which decreased the compressive strength of the bricks. Based on the results obtained, the
optimum amounts of waste were 9 wt. % sawdust of eucalyptus, 24 wt. % shaping moisture and 1.6 particle size diameter. These percentages produced bricks whose mechanical properties were
suitable for use as secondary raw materials in ceramic brick
	%P 2521 - 2525