	%T Mechanical and Chemical Properties of Zn-Ni-Al2O3 Nanocomposite Coatings
	%U https://publications.waset.org/pdf/10001993
	%V 104
	%X Zn alloy and composite coatings are widely used in
buildings and structures, automobile and fasteners industries to
protect steel component from corrosion. In this paper, Zn-Ni-Al2O3
nanocomposite coatings were electrodeposited on mild steel using a
novel sol enhanced electroplating method. In this method, transparent
Al2O3 sol was added into the acidic Zn-Ni bath to produced Zn-Ni-
Al2O3 nanocomposite coatings. The effect of alumina sol on the
electrodeposition process, and coating properties was investigated
using cyclic voltammetry, XRD, ESEM and Tafel test. Results from
XRD tests showed that the structure of all coatings was single γ-
Ni5Zn21 phase. Cyclic voltammetry results showed that the
electrodeposition overpotential was lower in the presence of alumina
sol in the bath, and caused the reduction potential of Zn-Ni to shift to
more positive values. Zn-Ni-Al2O3 nanocomposite coatings produced
more uniform and compact deposits, with fine grained microstructure
when compared to Zn-Ni coatings. The corrosion resistance of Zn-Ni
coatings was improved significantly by incorporation of alumina
nanoparticles into the coatings.