%0 Journal Article
	%A P. Selva and  B. Lorrain and  J. Alexis and  A. Seror and  A. Longuet and  C. Mary and  F. Denard
	%D 2015
	%J International Journal of Mechanical and Mechatronics Engineering
	%B World Academy of Science, Engineering and Technology
	%I Open Science Index 100, 2015
	%T Multiaxial Fatigue Analysis of a High Performance Nickel-Based Superalloy
	%U https://publications.waset.org/pdf/10000948
	%V 100
	%X Over the past four decades, the fatigue behavior of
nickel-based alloys has been widely studied. However, in recent
years, significant advances in the fabrication process leading to grain
size reduction have been made in order to improve fatigue properties
of aircraft turbine discs. Indeed, a change in particle size affects the
initiation mode of fatigue cracks as well as the fatigue life of the
material. The present study aims to investigate the fatigue behavior of
a newly developed nickel-based superalloy under biaxial-planar
loading. Low Cycle Fatigue (LCF) tests are performed at different
stress ratios so as to study the influence of the multiaxial stress state
on the fatigue life of the material. Full-field displacement and strain
measurements as well as crack initiation detection are obtained using
Digital Image Correlation (DIC) techniques. The aim of this
presentation is first to provide an in-depth description of both the
experimental set-up and protocol: the multiaxial testing machine, the
specific design of the cruciform specimen and performances of the
DIC code are introduced. Second, results for sixteen specimens
related to different load ratios are presented. Crack detection, strain
amplitude and number of cycles to crack initiation vs. triaxial stress
ratio for each loading case are given. Third, from fractographic
investigations by scanning electron microscopy it is found that the
mechanism of fatigue crack initiation does not depend on the triaxial
stress ratio and that most fatigue cracks initiate from subsurface
carbides.

	%P 544 - 549