	  title     = {Effect of High-Energy Ball Milling on the Electrical and Piezoelectric Properties of (K0.5Na0.5)(Nb0.9Ta0.1)O3 Lead-Free Piezoceramics},
	  author    = {Chongtham Jiten and  K. Chandramani Singh and  Radhapiyari Laishram},
	  country	= {},
	  institution	= {},
	  abstract     = {Nanocrystalline powders of the lead-free piezoelectric
material, tantalum-substituted potassium sodium niobate
(K0.5Na0.5)(Nb0.9Ta0.1)O3 (KNNT), were produced using a Retsch
PM100 planetary ball mill by setting the milling time to 15h, 20h,
25h, 30h, 35h and 40h, at a fixed speed of 250rpm. The average
particle size of the milled powders was found to decrease from 12nm
to 3nm as the milling time increases from 15h to 25h, which is in
agreement with the existing theoretical model. An anomalous
increase to 98nm and then a drop to 3nm in the particle size were
observed as the milling time further increases to 30h and 40h
respectively. Various sizes of these starting KNNT powders were
used to investigate the effect of milling time on the microstructure,
dielectric properties, phase transitions and piezoelectric properties of
the resulting KNNT ceramics. The particle size of starting KNNT
was somewhat proportional to the grain size. As the milling time
increases from 15h to 25h, the resulting ceramics exhibit
enhancement in the values of relative density from 94.8% to 95.8%,
room temperature dielectric constant (εRT) from 878 to 1213, and
piezoelectric charge coefficient (d33) from 108pC/N to 128pC/N. For
this range of ceramic samples, grain size refinement suppresses the
maximum dielectric constant (εmax), shifts the Curie temperature (Tc)
to a lower temperature and the orthorhombic-tetragonal phase
transition (Tot) to a higher temperature. Further increase of milling
time from 25h to 40h produces a gradual degradation in the values of
relative density, εRT, and d33 of the resulting ceramics.
},
	    journal   = {International Journal of Materials and Metallurgical Engineering},
	  volume    = {9},
	  number    = {1},
	  year      = {2015},
	  pages     = {11 - 14},
	  ee        = {https://publications.waset.org/pdf/10000157},
	  url   	= {https://publications.waset.org/vol/97},
	  bibsource = {https://publications.waset.org/},
	  issn  	= {eISSN: 1307-6892},
	  publisher = {World Academy of Science, Engineering and Technology},
	  index 	= {Open Science Index 97, 2015},
	}