Publications

2 Mechanical Properties and Microstructural Properties of CrSiN Coating

Authors: Dhiflaoui Hafedh, Khlifi Kaouthar, Ben Cheikh Larbi Ahmed

Abstract:

The present study deals with the characterization of CrSiN coatings obtained by PVD magnetron sputtering systems. CrSiN films were deposited with different Si contents, in order to check the effect of at.% variation on the different properties of the Cr–N system. Coatings were characterized by scanning electron microscopy (SEM) for thickness measurements, X-ray diffraction. Surface morphology and the roughness characteristics were explored using AFM, Mechanicals properties, elastic and plastic deformation resistance of thin films were investigated using nanoindentation test. We observed that the Si addition improved the hardness and the Young’s modulus of the Cr–N system. Indeed, the hardness value is 18,56 GPa for CrSiN coatings. Besides, the Young’s modulus value is 224,22 GPa for CrSiN coatings for Si content of 1.2 at.%.

Keywords: thin film, PVD, mechanicals properties

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1530
1 Nanoindentation of Thin Films Prepared by Physical Vapor Deposition

Authors: Dhiflaoui Hafedh, Khlifi Kaouthar, Ben Cheikh Larbi Ahmed

Abstract:

These Monolayer and multilayer coatings of CrN and AlCrN deposited on 100Cr6 (AISI 52100) substrate by PVD magnetron sputtering system. The microstructures of the coatings were characterized using atomic force microscopy (AFM). The AFM analysis revealed the presence of domes and craters that are uniformly distributed over all surfaces of the various layers. Nanoindentation measurement of CrN coating showed maximum hardness (H) and modulus (E) of 14 GPa and 190 GPa, respectively. The measured H and E values of AlCrN coatings were found to be 30 GPa and 382 GPa, respectively. The improved hardness in both the coatings was attributed mainly to a reduction in crystallite size and decrease in surface roughness. The incorporation of Al into the CrN coatings has improved both hardness and Young’s modulus.

Keywords: Coatings, Hardness, nano-indentation, CrN/AlCrN

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1763

Abstracts

1 A Nanoindentation Study of Thin Film Prepared by Physical Vapor Deposition

Authors: Dhiflaoui Hafedh, Ben Cheikh Larbi Ahmed, Khlifi Kaouther

Abstract:

Monolayer and multilayer coatings of CrN and AlCrN deposited on 100Cr6 (AISI 52100) substrate by PVD magnetron sputtering system. The micro structures of the coatings were characterized using atomic force microscopy (AFM). The AFM analysis revealed the presence of domes and craters which are uniformly distributed over all surfaces of the various layers. Nano indentation measurement of CrN coating showed maximum hardness (H) and modulus (E) of 14 GPa and 240 GPa, respectively. The measured H and E values of AlCrN coatings were found to be 30 GPa and 382 GPa, respectively. The improved hardness in both the coatings was attributed mainly to a reduction in crystallite size and decrease in surface roughness. The incorporation of Al into the CrN coatings has improved both hardness and Young’s modulus.

Keywords: Hardness, Nanoindentation, CrN, AlCrN coatings

Procedia PDF Downloads 404