	  title     = {Tensile Behavior of Spheroidizing Heat Treated High Carbon Steel},
	  author    = {Seok Hong Min and  Tae Kwon Ha},
	  country	= {},
	  institution	= {},
	  abstract     = {Spheroidization heat treatment was conducted on the  SK85 high carbon steel sheets with various initial microstructures  obtained after cold rolling by various reduction ratios at a couple of  annealing temperatures. On the high carbon steel sheet with fine  pearlite microstructure, obtained by soaking at 800oC for 2hr in a box furnace and then annealing at 570oC for 5min in a salt bath furnace followed by water quenching, cold rolling was conducted by reduction ratios of 20, 30, and 40%. Heat treatment for spheroidization was carried out at 600 and 720oC for the various time intervals from 0.1 to 32 hrs. Area fraction of spheroidized cementite was measured with an image analyzer as a function of cold reduction ratios and duration times. Tensile tests were carried out at room temperature on the spheoidized high carbon steel.

 
},
	    journal   = {International Journal of Industrial and Manufacturing Engineering},
	  volume    = {8},
	  number    = {2},
	  year      = {2014},
	  pages     = {105 - 107},
	  ee        = {https://publications.waset.org/pdf/9997319},
	  url   	= {https://publications.waset.org/vol/86},
	  bibsource = {https://publications.waset.org/},
	  issn  	= {eISSN: 1307-6892},
	  publisher = {World Academy of Science, Engineering and Technology},
	  index 	= {Open Science Index 86, 2014},
	}