	%T Separation of Manganese and Cadmium from Cobalt Electrolyte Solution by Solvent Extraction
	%U https://publications.waset.org/pdf/14928
	%V 71
	%X Impurity metals such as manganese and cadmium
from high-tenor cobalt electrolyte solution were selectively removed
by solvent extraction method using Co-D2EHPA after converting the functional group of D2EHPA with Co2+ ions. The process parameters
such as pH, organic concentration, O/A ratio, kinetics etc. were
investigated and the experiments were conducted by batch tests in the laboratory bench scale. Results showed that a significant amount
of manganese and cadmium can be extracted using Co-D2EHPA for the optimum processing of cobalt electrolyte solution at equilibrium pH about 3.5. The McCabe-Thiele diagram, constructed from the
extraction studies showed that 100% impurities can be extracted through four stages for manganese and three stages for cadmium
using O/A ratio of 0.65 and 1.0, respectively. From the stripping study, it was found that 100% manganese and cadmium can be stripped from the loaded organic using 0.4 M H2SO4 in a single
contact. The loading capacity of Co-D2EHPA by manganese and cadmium were also investigated with different O/A ratio as well as
with number of stages of contact of aqueous and organic phases. Valuable information was obtained for the designing of an impurities
removal process for the production of pure cobalt with less trouble in the electrowinning circuit.