Static Recrystallization Behavior of Mg Alloy Single Crystals

Authors: Joon Ho Kim, Jae Ho Choi, Tae Kwon Ha

Abstract:

Single crystals of Magnesium alloys such as pure Mg, Mg-1Zn-0.5Y, Mg-0.1Y, and Mg-0.1Ce alloys were successfully fabricated in this study by employing the modified Bridgman method. To determine the exact orientation of crystals, pole figure measurement using X-ray diffraction were carried out on each single crystal. Hardness and compression tests were conducted followed by subsequent recrysatllization annealing. Recrystallization kinetics of Mg alloy single crystals has been investigated. Fabricated single crystals were cut into rectangular shaped specimen and solution treated at 400oC for 24 hrs, and then deformed in compression mode by 30% reduction. Annealing treatment for recrystallization has been conducted on these cold-rolled plates at temperatures of 300oC for various times from 1 to 20 mins. The microstructure observation and hardness measurement conducted on the recrystallized specimens revealed that static recrystallization of ternary alloy single crystal was very slow, while recrystallization behavior of binary alloy single crystals appeared to be very fast.

Keywords: Magnesium, Mg-rare earth alloys, compression test, static recrystallization, hardness.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1083661

References:

[1] W. Qiu, E-H. Han, L. Liu, Trans. Nonferrous Met. Soc. China, vol. 20, p. 481. 2010.
[2] S. M. Masoudpanah, R. Mahmudi, Mater. Sci. & Eng. A, vol. 526, p. 22. 2009.
[3] Y. Wang, S. Guan, X. Zeng, W. Ding, Mater. Sci. & Eng. A, vol. 416, p. 109. 2006.
[4] M. R. Barnett, M.D. Nave, C.J. Bettles, Mater. Sci. & Eng. A, vol. 386, p. 205, 2004.
[5] E. Schmid, Z. Elektrochem, vol. 37, p.447, 1931.
[6] A. Beck, "The technology of Magnesium and Its Alloys", Huges, London, p. 22, 1940.
[7] N.-J. Park, S.-H. Han: Kor. J. Met. Mater. vol. 48, pp. 498-505, 2010.