%0 Journal Article
	%A Chaiyakrit Raoupatham and  Ram Hari Dhakal and  Chalermchai Wanichlamlert
	%D 2015
	%J International Journal of Civil and Environmental Engineering
	%B World Academy of Science, Engineering and Technology
	%I Open Science Index 108, 2015
	%T Estimation Model for Concrete Slump Recovery by Using Superplasticizer
	%U https://publications.waset.org/pdf/10003133
	%V 108
	%X This paper aimed to introduce the solution of concrete
slump recovery using chemical admixture type-F (superplasticizer,
naphthalene base) to the practice in order to solve unusable concrete
problem due to concrete loss its slump, especially for those tropical
countries that have faster slump loss rate. In the other hand, randomly
adding superplasticizer into concrete can cause concrete to segregate.
Therefore, this paper also develops the estimation model used to
calculate amount of second dose of superplasticizer need for concrete
slump recovery. Fresh properties of ordinary Portland cement
concrete with volumetric ratio of paste to void between aggregate
(paste content) of 1.1-1.3 with water-cement ratio zone of 0.30 to
0.67 and initial superplasticizer (naphthalene base) of 0.25%-1.6%
were tested for initial slump and slump loss for every 30 minutes for
one and half hour by slump cone test. Those concretes with slump
loss range from 10% to 90% were re-dosed and successfully
recovered back to its initial slump. Slump after re-dosed was tested
by slump cone test. From the result, it has been concluded that, slump
loss was slower for those mix with high initial dose of
superplasticizer due to addition of superplasticizer will disturb
cement hydration. The required second dose of superplasticizer was
affected by two major parameters, which were water-cement ratio
and paste content, where lower water-cement ratio and paste content
cause an increase in require second dose of superplasticizer. The
amount of second dose of superplasticizer is higher as the solid
content within the system is increase, solid can be either from cement
particles or aggregate. The data was analyzed to form an equation use
to estimate the amount of second dosage requirement of
superplasticizer to recovery slump to its original.
	%P 1588 - 1593